INFLUENCE OF SIZE INPUT RAW MATERIALS OF THE RESULTING BRITTLE-FRACTURE PROPERTIES OF VITREOUS ENAMEL COATINGS
Identifikátory výsledku
Kód výsledku v IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F61989100%3A27230%2F11%3A86080484" target="_blank" >RIV/61989100:27230/11:86080484 - isvavai.cz</a>
Nalezeny alternativní kódy
RIV/61989100:27360/11:86080484
Výsledek na webu
—
DOI - Digital Object Identifier
—
Alternativní jazyky
Jazyk výsledku
angličtina
Název v původním jazyce
INFLUENCE OF SIZE INPUT RAW MATERIALS OF THE RESULTING BRITTLE-FRACTURE PROPERTIES OF VITREOUS ENAMEL COATINGS
Popis výsledku v původním jazyce
Vitreous enamel coatings are surface treatments which occur on metallic substrates by burning at a temperature above 800°C. These coatings provide good protection for metal materials against corrosion, aggressive environments and also significantly improve the surface properties of basic material. The resistance of the enamel coating to cracking and fracture can significantly reduce the risk of defects such as ?fish scales?, chipping, cracking, etc. Vitreous coatings are widely used in many technology sectors (construction, engineering, architecture, medicine, food industry, chemical industry, etc). The most important inorganic components in the manufacture of these coatings are glassy frit, pigments and clay. Usage of different sizes of inorganic components has a large influence on the quality of the final coating. The size of the input components of inorganic nano-sized particles positively impacts the brittle-fracture properties of the vitreous enamel coating compared to conventiona
Název v anglickém jazyce
INFLUENCE OF SIZE INPUT RAW MATERIALS OF THE RESULTING BRITTLE-FRACTURE PROPERTIES OF VITREOUS ENAMEL COATINGS
Popis výsledku anglicky
Vitreous enamel coatings are surface treatments which occur on metallic substrates by burning at a temperature above 800°C. These coatings provide good protection for metal materials against corrosion, aggressive environments and also significantly improve the surface properties of basic material. The resistance of the enamel coating to cracking and fracture can significantly reduce the risk of defects such as ?fish scales?, chipping, cracking, etc. Vitreous coatings are widely used in many technology sectors (construction, engineering, architecture, medicine, food industry, chemical industry, etc). The most important inorganic components in the manufacture of these coatings are glassy frit, pigments and clay. Usage of different sizes of inorganic components has a large influence on the quality of the final coating. The size of the input components of inorganic nano-sized particles positively impacts the brittle-fracture properties of the vitreous enamel coating compared to conventiona
Klasifikace
Druh
D - Stať ve sborníku
CEP obor
JK - Koroze a povrchové úpravy materiálu
OECD FORD obor
—
Návaznosti výsledku
Projekt
<a href="/cs/project/ME08083" target="_blank" >ME08083: Komplexní systém krátkodobé a dlouhodobé antikorozní ochrany materiálů hutní produkce</a><br>
Návaznosti
P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)
Ostatní
Rok uplatnění
2011
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů
Údaje specifické pro druh výsledku
Název statě ve sborníku
20th Anniversary International Conference on Metallurgy and Materials: METAL 2011
ISBN
978-80-87294-24-6
ISSN
—
e-ISSN
—
Počet stran výsledku
5
Strana od-do
83-84
Název nakladatele
Tanger
Místo vydání
Ostrava
Místo konání akce
Brno
Datum konání akce
18. 5. 2011
Typ akce podle státní příslušnosti
WRD - Celosvětová akce
Kód UT WoS článku
—