Influence size of clay inorganic components on brittle fracture properties of vitreous enamel coatings

Popis výsledku v původním jazyce

Corrosion of metals depreciates the products by physic-chemical working of surrounding environment. Vitreous enamel coating is surface treatment, which ensure not only perfect protection of materials against corrosion, but also give for surface of basicmaterial the exceptional properties. We can use this coating in energy-, ecological-, agricultural- engineering, further in architecture-building industries and on products of commodity. Vitreous enamel coats are glassy inorganic coatings created on metal substrate by the process of burning at temperature above 800 °C. Resulting brittle-fracture properties of the coating depend on its structure, texture and chemical compound and on influence of the properties metal substrate. Most important inorganic components at production of these coatings are clay and vitreous fritted glass. Using of different grain size of these components has influence on final quality of coating. Principal aim of this work was comparison of brittle-fracture prope

Název v anglickém jazyce

Influence size of clay inorganic components on brittle fracture properties of vitreous enamel coatings

Popis výsledku anglicky

Corrosion of metals depreciates the products by physic-chemical working of surrounding environment. Vitreous enamel coating is surface treatment, which ensure not only perfect protection of materials against corrosion, but also give for surface of basicmaterial the exceptional properties. We can use this coating in energy-, ecological-, agricultural- engineering, further in architecture-building industries and on products of commodity. Vitreous enamel coats are glassy inorganic coatings created on metal substrate by the process of burning at temperature above 800 °C. Resulting brittle-fracture properties of the coating depend on its structure, texture and chemical compound and on influence of the properties metal substrate. Most important inorganic components at production of these coatings are clay and vitreous fritted glass. Using of different grain size of these components has influence on final quality of coating. Principal aim of this work was comparison of brittle-fracture prope

Druh

D - Stať ve sborníku

CEP obor

BM - Fyzika pevných látek a magnetismus

OECD FORD obor

—

Projekt

<a href="/cs/project/KAN400100653" target="_blank" >KAN400100653: Samoorganizované magnetické nanostruktury</a><br>

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)

Rok uplatnění

2008

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název statě ve sborníku

Sborník přednášek

ISBN

978-80-254-1987-8

ISSN

—

e-ISSN

—

Počet stran výsledku

1

Strana od-do

—

Název nakladatele

TANGER, spol.s r.o.

Místo vydání

Ostrava

Místo konání akce

Hradec nad Moravicí, Česká republika

Datum konání akce

13. 5. 2008

Typ akce podle státní příslušnosti

WRD - Celosvětová akce

Kód UT WoS článku

—