Vliv velikosti částic jílu na funkční vlastnosti sklovitých smaltových povlaků.

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F61989100%3A27350%2F08%3A00019860" target="_blank" >RIV/61989100:27350/08:00019860 - isvavai.cz</a>

Výsledek na webu

—

DOI - Digital Object Identifier

—

Jazyk výsledku

angličtina

Název v původním jazyce

An effect of clay particles size on funkcional features of vitreous enamel coatings.

Popis výsledku v původním jazyce

Vitreous enamel coats are glassy inorganic coatings created on metal substrate by the process of burning at temperature above 800 °C. We can use this coating in assorted engineering. Creating a compact enamel coat (without faults which would penetrate tothe foundation metal and damage the compactness of the enamel) is the essential precondition for using its functional properties. Most important inorganic components at production of these coatings are clay and vitreous fritted glass. Using of differentgrain size of these components has influence on final quality of coating. Principal aim of this project was comparison of brittle-fracture properties of glass ceramics coatings, created by the help of inorganic components in ordinarily used size and inorganic components grinded to nano-size.

Název v anglickém jazyce

An effect of clay particles size on funkcional features of vitreous enamel coatings.

Popis výsledku anglicky

Vitreous enamel coats are glassy inorganic coatings created on metal substrate by the process of burning at temperature above 800 °C. We can use this coating in assorted engineering. Creating a compact enamel coat (without faults which would penetrate tothe foundation metal and damage the compactness of the enamel) is the essential precondition for using its functional properties. Most important inorganic components at production of these coatings are clay and vitreous fritted glass. Using of differentgrain size of these components has influence on final quality of coating. Principal aim of this project was comparison of brittle-fracture properties of glass ceramics coatings, created by the help of inorganic components in ordinarily used size and inorganic components grinded to nano-size.

Druh

J_x - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)

CEP obor

BM - Fyzika pevných látek a magnetismus

OECD FORD obor

—

Projekt

<a href="/cs/project/KAN400100653" target="_blank" >KAN400100653: Samoorganizované magnetické nanostruktury</a><br>

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)

Rok uplatnění

2008

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

Acta Mechanica Slovaca

ISSN

1335-2393

e-ISSN

—

Svazek periodika

12

Číslo periodika v rámci svazku

4-B

Stát vydavatele periodika

SK - Slovenská republika

Počet stran výsledku

6

Strana od-do

—

Kód UT WoS článku

—

EID výsledku v databázi Scopus

—