Analysis of the Zinc Layer on Steel Products with Varying Silicon Content

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F61989100%3A27230%2F17%3A10238015" target="_blank" >RIV/61989100:27230/17:10238015 - isvavai.cz</a>

Nalezeny alternativní kódy

RIV/61989100:27360/17:10238015

Výsledek na webu

—

DOI - Digital Object Identifier

—

Jazyk výsledku

angličtina

Název v původním jazyce

Analysis of the Zinc Layer on Steel Products with Varying Silicon Content

Popis výsledku v původním jazyce

This work experimentally evaluates the effects of chemical composition, particularly the amount of silicon on the quality of the applied coating technology of hot dip galvanizing. The experiment is aimed at determining the microstructure, thickness and quality of the zinc layer on the test samples of different steel grades. For the experiment there were selected structural steels S235JR and S355J2 with low silicon content. High strength steel S690QL with higher silicon content was chosen for comparison. Results of independent measurements of coating thickness using optical microscopy and magnetic method indicate only minimal differences between steel S235JR and S355J2. Steel S690QL exhibits thick and uneven layer of the zinc. Steel S690QL should be evaluated as unsatisfactory type of steel for hot-dip galvanizing.

Název v anglickém jazyce

Analysis of the Zinc Layer on Steel Products with Varying Silicon Content

Popis výsledku anglicky

This work experimentally evaluates the effects of chemical composition, particularly the amount of silicon on the quality of the applied coating technology of hot dip galvanizing. The experiment is aimed at determining the microstructure, thickness and quality of the zinc layer on the test samples of different steel grades. For the experiment there were selected structural steels S235JR and S355J2 with low silicon content. High strength steel S690QL with higher silicon content was chosen for comparison. Results of independent measurements of coating thickness using optical microscopy and magnetic method indicate only minimal differences between steel S235JR and S355J2. Steel S690QL exhibits thick and uneven layer of the zinc. Steel S690QL should be evaluated as unsatisfactory type of steel for hot-dip galvanizing.

Druh

D - Stať ve sborníku

CEP obor

—

OECD FORD obor

20506 - Coating and films

Projekt

<a href="/cs/project/LO1203" target="_blank" >LO1203: Regionální materiálově technologické výzkumné centrum - Program udržitelnosti</a><br>

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)

Rok uplatnění

2017

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název statě ve sborníku

METAL 2017: conference proceedings : 26th International Conference on Metallurgy and Materials : (reviewed version) : May 24th-26th 2017, Hotel Voroněž I, Brno, Czech Republic, EU

ISBN

978-80-87294-79-6

ISSN

—

e-ISSN

neuvedeno

Počet stran výsledku

6

Strana od-do

"1456 – 1461"

Název nakladatele

Tanger

Místo vydání

Ostrava

Místo konání akce

Brno

Datum konání akce

24. 5. 2017

Typ akce podle státní příslušnosti

WRD - Celosvětová akce

Kód UT WoS článku

—