Use of GDOES method for evaluation of the quality and thickness of hot dip galvanised coating
Identifikátory výsledku
Kód výsledku v IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F61989100%3A27230%2F18%3A10240865" target="_blank" >RIV/61989100:27230/18:10240865 - isvavai.cz</a>
Nalezeny alternativní kódy
RIV/61989100:27360/18:10240865
Výsledek na webu
<a href="https://www.tandfonline.com/doi/abs/10.1080/00202967.2018.1520531?journalCode=ytim20" target="_blank" >https://www.tandfonline.com/doi/abs/10.1080/00202967.2018.1520531?journalCode=ytim20</a>
DOI - Digital Object Identifier
<a href="http://dx.doi.org/10.1080/00202967.2018.1520531" target="_blank" >10.1080/00202967.2018.1520531</a>
Alternativní jazyky
Jazyk výsledku
angličtina
Název v původním jazyce
Use of GDOES method for evaluation of the quality and thickness of hot dip galvanised coating
Popis výsledku v původním jazyce
The paper describes an assessment of thickness and quality of hot-dip galvanised coating by means of the glow discharge optical emission spectrometry method (GDOES). For comparison, a metallographic analysis was made using an optical microscope. An important factor influencing thickness and quality of the hot-dip galvanised coating is chemical composition of steel, particularly the amounts of silicon. Structural steels with a low amount of silicon S235JR and S355J2 were chosen for the experiment and high-strength steel S690QL with a high amount of silicon was chosen for comparative purposes. The results of the coating thickness measurement by means of GDOES and optical microscopy show only minimal differences. Steel S690QL shows a thick and uneven zinc coating. In the case of steels S235JR and S355J2 an optimal hot-dip galvanised coating was observed.
Název v anglickém jazyce
Use of GDOES method for evaluation of the quality and thickness of hot dip galvanised coating
Popis výsledku anglicky
The paper describes an assessment of thickness and quality of hot-dip galvanised coating by means of the glow discharge optical emission spectrometry method (GDOES). For comparison, a metallographic analysis was made using an optical microscope. An important factor influencing thickness and quality of the hot-dip galvanised coating is chemical composition of steel, particularly the amounts of silicon. Structural steels with a low amount of silicon S235JR and S355J2 were chosen for the experiment and high-strength steel S690QL with a high amount of silicon was chosen for comparative purposes. The results of the coating thickness measurement by means of GDOES and optical microscopy show only minimal differences. Steel S690QL shows a thick and uneven zinc coating. In the case of steels S235JR and S355J2 an optimal hot-dip galvanised coating was observed.
Klasifikace
Druh
J<sub>imp</sub> - Článek v periodiku v databázi Web of Science
CEP obor
—
OECD FORD obor
20506 - Coating and films
Návaznosti výsledku
Projekt
<a href="/cs/project/LO1203" target="_blank" >LO1203: Regionální materiálově technologické výzkumné centrum - Program udržitelnosti</a><br>
Návaznosti
P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)<br>S - Specificky vyzkum na vysokych skolach
Ostatní
Rok uplatnění
2018
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů
Údaje specifické pro druh výsledku
Název periodika
Transactions of the Institute of Metal Finishing
ISSN
0020-2967
e-ISSN
—
Svazek periodika
96
Číslo periodika v rámci svazku
6
Stát vydavatele periodika
US - Spojené státy americké
Počet stran výsledku
6
Strana od-do
313-318
Kód UT WoS článku
000447137500007
EID výsledku v databázi Scopus
2-s2.0-85054908219