Complex material and surface analysis of anterolateral distal tibial plate of 1.4441 steel

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F61989100%3A27230%2F21%3A10249114" target="_blank" >RIV/61989100:27230/21:10249114 - isvavai.cz</a>

Nalezeny alternativní kódy

RIV/61989100:27360/21:10249114 RIV/61989100:27690/21:10249114 RIV/00843989:_____/22:E0109448 RIV/61988987:17110/22:A2302FLU

Výsledek na webu

<a href="https://www.researchgate.net/publication/357371720_Complex_Material_and_Surface_Analysis_of_Anterolateral_Distal_Tibial_Plate_of_14441_Steel" target="_blank" >https://www.researchgate.net/publication/357371720_Complex_Material_and_Surface_Analysis_of_Anterolateral_Distal_Tibial_Plate_of_14441_Steel</a>

DOI - Digital Object Identifier

<a href="http://dx.doi.org/10.3390/met12010060" target="_blank" >10.3390/met12010060</a>

Jazyk výsledku

angličtina

Název v původním jazyce

Complex material and surface analysis of anterolateral distal tibial plate of 1.4441 steel

Popis výsledku v původním jazyce

Nickel-based austenitic stainless steels are still common for manufacture of implants intended for acute hard tissue reinforcement or stabilization, but the risk of negative reactions due to soluble nickel-rich corrosion products must be considered seriously. Corrosion processes may even be accelerated by the evolution of microstructure caused by excessive heat during machining, etc. Therefore, this study also deals with the investigation of microstructure and microhardness changes near the threaded holes of the anterolateral distal tibial plate containing approx. 14wt.% Ni by composition. There were only insignificant changes of microhardness, grain size, or microstructure orientation found close to the area of machining. In addition, wettability measurements of surface energy demonstrated only minor differences for bulk material and areas close to machining. The cyclic potentiodynamic polarization tests were performed in isotonic physiological solution. The first cycle was used for the determination of corrosion characteristics of the implant after chemical passivation, the second cycle was used to simulate real material behavior under the condition of previous surface damage by excessive pitting corrosion occurring during previous polarization. It was found that the damaged and spontaneously repassived surface showed a three-time higher standard corrosion rate than the &quot;as received&quot; chemically passivated surface. One may conclude that previous surface damage may decrease the lifetime of the implant significantly and increase the amount of nickel-based corrosion products distributed into surrounding tissues. (C) 2021 by the authors. Licensee MDPI, Basel, Switzerland.

Název v anglickém jazyce

Complex material and surface analysis of anterolateral distal tibial plate of 1.4441 steel

Popis výsledku anglicky

Nickel-based austenitic stainless steels are still common for manufacture of implants intended for acute hard tissue reinforcement or stabilization, but the risk of negative reactions due to soluble nickel-rich corrosion products must be considered seriously. Corrosion processes may even be accelerated by the evolution of microstructure caused by excessive heat during machining, etc. Therefore, this study also deals with the investigation of microstructure and microhardness changes near the threaded holes of the anterolateral distal tibial plate containing approx. 14wt.% Ni by composition. There were only insignificant changes of microhardness, grain size, or microstructure orientation found close to the area of machining. In addition, wettability measurements of surface energy demonstrated only minor differences for bulk material and areas close to machining. The cyclic potentiodynamic polarization tests were performed in isotonic physiological solution. The first cycle was used for the determination of corrosion characteristics of the implant after chemical passivation, the second cycle was used to simulate real material behavior under the condition of previous surface damage by excessive pitting corrosion occurring during previous polarization. It was found that the damaged and spontaneously repassived surface showed a three-time higher standard corrosion rate than the &quot;as received&quot; chemically passivated surface. One may conclude that previous surface damage may decrease the lifetime of the implant significantly and increase the amount of nickel-based corrosion products distributed into surrounding tissues. (C) 2021 by the authors. Licensee MDPI, Basel, Switzerland.

Druh

J_imp - Článek v periodiku v databázi Web of Science

CEP obor

—

OECD FORD obor

20501 - Materials engineering

Projekt

<a href="/cs/project/EF17_049%2F0008441" target="_blank" >EF17_049/0008441: Inovativní léčebné metody pohybového aparátu v úrazové chirurgii</a><br>

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)<br>S - Specificky vyzkum na vysokych skolach

Rok uplatnění

2021

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

Metals

ISSN

2075-4701

e-ISSN

—

Svazek periodika

12

Číslo periodika v rámci svazku

1

Stát vydavatele periodika

CH - Švýcarská konfederace

Počet stran výsledku

15

Strana od-do

—

Kód UT WoS článku

000747770300001

EID výsledku v databázi Scopus

2-s2.0-85121754066