The effect of machining parameters on surface integrity and fatigue performance of 42CrMo4+QT high-strength steel
Identifikátory výsledku
Kód výsledku v IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F61989100%3A27230%2F25%3A10260033" target="_blank" >RIV/61989100:27230/25:10260033 - isvavai.cz</a>
Výsledek na webu
<a href="https://journals.sagepub.com/doi/full/10.1177/02670836251362509" target="_blank" >https://journals.sagepub.com/doi/full/10.1177/02670836251362509</a>
DOI - Digital Object Identifier
<a href="http://dx.doi.org/10.1177/02670836251362509" target="_blank" >10.1177/02670836251362509</a>
Alternativní jazyky
Jazyk výsledku
angličtina
Název v původním jazyce
The effect of machining parameters on surface integrity and fatigue performance of 42CrMo4+QT high-strength steel
Popis výsledku v původním jazyce
This study investigates how machining parameters affect surface integrity and fatigue performance in 42CrMo4 + QT steel. Nine turning setups were tested to evaluate surface roughness, residual stresses, and fatigue strength. Fatigue testing under fully reversed loading (R = -1) at similar to 150 Hz revealed that the best fatigue performance occurred in the setup with a cutting speed of 100 m/min, feed rate of 0.1 mm/min, tool nose radius of 0.4 mm, 0.3 mm total finishing depth (over three cuts), and coolant applied. Cutting speed showed the clearest benefit, while other parameters had less predictable effects. Surface roughness did not consistently correlate with fatigue life. Overall, selected machining parameters strongly influence fatigue behavior, though roughness and residual stresses alone do not fully explain the performance trends observed.
Název v anglickém jazyce
The effect of machining parameters on surface integrity and fatigue performance of 42CrMo4+QT high-strength steel
Popis výsledku anglicky
This study investigates how machining parameters affect surface integrity and fatigue performance in 42CrMo4 + QT steel. Nine turning setups were tested to evaluate surface roughness, residual stresses, and fatigue strength. Fatigue testing under fully reversed loading (R = -1) at similar to 150 Hz revealed that the best fatigue performance occurred in the setup with a cutting speed of 100 m/min, feed rate of 0.1 mm/min, tool nose radius of 0.4 mm, 0.3 mm total finishing depth (over three cuts), and coolant applied. Cutting speed showed the clearest benefit, while other parameters had less predictable effects. Surface roughness did not consistently correlate with fatigue life. Overall, selected machining parameters strongly influence fatigue behavior, though roughness and residual stresses alone do not fully explain the performance trends observed.
Klasifikace
Druh
J<sub>imp</sub> - Článek v periodiku v databázi Web of Science
CEP obor
—
OECD FORD obor
20501 - Materials engineering
Návaznosti výsledku
Projekt
—
Návaznosti
S - Specificky vyzkum na vysokych skolach
Ostatní
Rok uplatnění
2025
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů
Údaje specifické pro druh výsledku
Název periodika
Materials Science and Technology
ISSN
0267-0836
e-ISSN
1743-2847
Svazek periodika
2025
Číslo periodika v rámci svazku
2025
Stát vydavatele periodika
GB - Spojené království Velké Británie a Severního Irska
Počet stran výsledku
20
Strana od-do
nestránkováno
Kód UT WoS článku
001539513500001
EID výsledku v databázi Scopus
—