Enhanced electrical conductivity of polyaniline films by postsynthetic DC high-voltage electrical field treatment

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F61989100%3A27240%2F13%3A86086147" target="_blank" >RIV/61989100:27240/13:86086147 - isvavai.cz</a>

Nalezeny alternativní kódy

RIV/61989100:27360/13:86088362 RIV/61989100:27640/13:86086147 RIV/44555601:13440/13:43885028

Výsledek na webu

<a href="http://dx.doi.org/10.1016/j.synthmet.2013.07.024" target="_blank" >http://dx.doi.org/10.1016/j.synthmet.2013.07.024</a>

DOI - Digital Object Identifier

<a href="http://dx.doi.org/10.1016/j.synthmet.2013.07.024" target="_blank" >10.1016/j.synthmet.2013.07.024</a>

Jazyk výsledku

angličtina

Název v původním jazyce

Enhanced electrical conductivity of polyaniline films by postsynthetic DC high-voltage electrical field treatment

Popis výsledku v původním jazyce

New approach of chemical bath deposition combined with drying of freshly polymerized PANI films in DC high-voltage static electrical field 0.6-2.7 kV/cm has been applied in present work. AFM and SEM microscopy revealed the significant changes of structure and morphology of PANI films, however the most important result of high-voltage treatment was the strong increase of conductivity of PANI films from 88 S/m for the reference sample untreated in high-voltage field up to 374 S/m for samples dried in theelectric field (1.0 kV/cm). The dependence of PANI conductivity on the intensity of high-voltage field showed the maximum conductivity for 1.0 kV/cm. Effects of corona discharge observed for high-voltage field intensity above 2.0 kV/cm on the samples arealso presented. Results showed the possibility to change the nanostructure, morphology and conductivity using high-voltage electrical field.

Název v anglickém jazyce

Enhanced electrical conductivity of polyaniline films by postsynthetic DC high-voltage electrical field treatment

Popis výsledku anglicky

New approach of chemical bath deposition combined with drying of freshly polymerized PANI films in DC high-voltage static electrical field 0.6-2.7 kV/cm has been applied in present work. AFM and SEM microscopy revealed the significant changes of structure and morphology of PANI films, however the most important result of high-voltage treatment was the strong increase of conductivity of PANI films from 88 S/m for the reference sample untreated in high-voltage field up to 374 S/m for samples dried in theelectric field (1.0 kV/cm). The dependence of PANI conductivity on the intensity of high-voltage field showed the maximum conductivity for 1.0 kV/cm. Effects of corona discharge observed for high-voltage field intensity above 2.0 kV/cm on the samples arealso presented. Results showed the possibility to change the nanostructure, morphology and conductivity using high-voltage electrical field.

Druh

J_x - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)

CEP obor

JJ - Ostatní materiály

OECD FORD obor

—

Projekt

<a href="/cs/project/GAP108%2F11%2F1057" target="_blank" >GAP108/11/1057: Příprava, struktura a vlastnosti nanokompozitů vodivý polymer/fylosilikát</a><br>

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)

Rok uplatnění

2013

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

Synthetic Metals

ISSN

0379-6779

e-ISSN

—

Svazek periodika

179

Číslo periodika v rámci svazku

1. září 2013

Stát vydavatele periodika

US - Spojené státy americké

Počet stran výsledku

6

Strana od-do

116-121

Kód UT WoS článku

000324969100014

EID výsledku v databázi Scopus

—