Electrically conductive and transparent PANI/montmorillonite nanocomposite thin films

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F61989100%3A27710%2F14%3A86092180" target="_blank" >RIV/61989100:27710/14:86092180 - isvavai.cz</a>

Výsledek na webu

<a href="http://dx.doi.org/10.1016/j.tsf.2014.05.006" target="_blank" >http://dx.doi.org/10.1016/j.tsf.2014.05.006</a>

DOI - Digital Object Identifier

<a href="http://dx.doi.org/10.1016/j.tsf.2014.05.006" target="_blank" >10.1016/j.tsf.2014.05.006</a>

Jazyk výsledku

angličtina

Název v původním jazyce

Electrically conductive and transparent PANI/montmorillonite nanocomposite thin films

Popis výsledku v původním jazyce

Simple technology (i.e. one-step polymerization of anilinium sulfate in the presence of montmorillonite) have been used to prepare the polyaniline/montmorillonite (PANI/MMT) nanocomposite thin films. Present work is focused on the effect of MMT content on the thickness, morphology and electrical conductivity of PANI/MMT nanocomposite films. Increase of MMT content led to the increase of film thickness and surface roughness and decrease of conductivity from maximum value 356 S/m to minimum value 76 S/m,while for pure PANI films, prepared using the same polymerization procedure (from anilinium sulfate) the conductivity was 59 S/m. On the other hand the MMT content exhibited significant impact on the optical transparency of PANI/MMT nanocomposite films,which was limited to the range 450 - 650 nm in contrast with pure PANI films showing the nonzero transparency in the whole measured range of wavelength 300-800 nm. AFM images clearly proved the alignment of PANI chains in nanocomposite fi

Název v anglickém jazyce

Electrically conductive and transparent PANI/montmorillonite nanocomposite thin films

Popis výsledku anglicky

Simple technology (i.e. one-step polymerization of anilinium sulfate in the presence of montmorillonite) have been used to prepare the polyaniline/montmorillonite (PANI/MMT) nanocomposite thin films. Present work is focused on the effect of MMT content on the thickness, morphology and electrical conductivity of PANI/MMT nanocomposite films. Increase of MMT content led to the increase of film thickness and surface roughness and decrease of conductivity from maximum value 356 S/m to minimum value 76 S/m,while for pure PANI films, prepared using the same polymerization procedure (from anilinium sulfate) the conductivity was 59 S/m. On the other hand the MMT content exhibited significant impact on the optical transparency of PANI/MMT nanocomposite films,which was limited to the range 450 - 650 nm in contrast with pure PANI films showing the nonzero transparency in the whole measured range of wavelength 300-800 nm. AFM images clearly proved the alignment of PANI chains in nanocomposite fi

Druh

J_x - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)

CEP obor

JI - Kompositní materiály

OECD FORD obor

—

Projekt

Výsledek vznikl pri realizaci vícero projektů. Více informací v záložce Projekty.

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)<br>S - Specificky vyzkum na vysokych skolach

Rok uplatnění

2014

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

Thin Solid Films

ISSN

0040-6090

e-ISSN

—

Svazek periodika

562

Číslo periodika v rámci svazku

neuveden

Stát vydavatele periodika

NL - Nizozemsko

Počet stran výsledku

7

Strana od-do

319-325

Kód UT WoS článku

000340658100050

EID výsledku v databázi Scopus

—