Properties of polyaniline/montmorillonite thin films in dependence on preparation temperature
Identifikátory výsledku
Kód výsledku v IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F61989100%3A27360%2F15%3A86095020" target="_blank" >RIV/61989100:27360/15:86095020 - isvavai.cz</a>
Nalezeny alternativní kódy
RIV/61989100:27740/15:86095020 RIV/61989100:27640/15:86095020
Výsledek na webu
<a href="http://konsys-t.tanger.cz/files/proceedings/20/reports/3067.pdf" target="_blank" >http://konsys-t.tanger.cz/files/proceedings/20/reports/3067.pdf</a>
DOI - Digital Object Identifier
—
Alternativní jazyky
Jazyk výsledku
angličtina
Název v původním jazyce
Properties of polyaniline/montmorillonite thin films in dependence on preparation temperature
Popis výsledku v původním jazyce
A simple method was used for the preparation of polyaniline/montmorillonite (PANI/MMT) nanocomposite thin films deposited on glass slides. Water solution of anilinium sulfate (as a precursor) was mixed with the ammonium peroxydisulfate (as an oxidizing agent) in presence of glass slide and an appropriate amount of MMT at different temperatures. Two following temperatures were used: 10oC and 20oC. Layered structure of the MMT significantly affects the ordering of PANI chains, i.e. the PANI nanostructure.PANI/MMT thin films contain no other components like additional polymeric carriers or binders. Present work is focused on how the change of temperature of preparation mixture affect the thickness, morphology and electrical conductivity of resulting PANI/MMT nanocomposite films. Raman spectroscopy, atomic force microscopy and conductivity measurement were used for the characterization of the samples.
Název v anglickém jazyce
Properties of polyaniline/montmorillonite thin films in dependence on preparation temperature
Popis výsledku anglicky
A simple method was used for the preparation of polyaniline/montmorillonite (PANI/MMT) nanocomposite thin films deposited on glass slides. Water solution of anilinium sulfate (as a precursor) was mixed with the ammonium peroxydisulfate (as an oxidizing agent) in presence of glass slide and an appropriate amount of MMT at different temperatures. Two following temperatures were used: 10oC and 20oC. Layered structure of the MMT significantly affects the ordering of PANI chains, i.e. the PANI nanostructure.PANI/MMT thin films contain no other components like additional polymeric carriers or binders. Present work is focused on how the change of temperature of preparation mixture affect the thickness, morphology and electrical conductivity of resulting PANI/MMT nanocomposite films. Raman spectroscopy, atomic force microscopy and conductivity measurement were used for the characterization of the samples.
Klasifikace
Druh
D - Stať ve sborníku
CEP obor
JI - Kompositní materiály
OECD FORD obor
—
Návaznosti výsledku
Projekt
<a href="/cs/project/ED1.1.00%2F02.0070" target="_blank" >ED1.1.00/02.0070: Centrum excelence IT4Innovations</a><br>
Návaznosti
P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)<br>S - Specificky vyzkum na vysokych skolach
Ostatní
Rok uplatnění
2015
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů
Údaje specifické pro druh výsledku
Název statě ve sborníku
NANOCON 2014: 6th International Conference, November 5th-7th 2014, Hotel Voronez I, Brno, Czech Republic, EU
ISBN
978-80-87294-53-6
ISSN
—
e-ISSN
—
Počet stran výsledku
5
Strana od-do
104-108
Název nakladatele
Tanger
Místo vydání
Ostrava
Místo konání akce
Brno
Datum konání akce
5. 11. 2014
Typ akce podle státní příslušnosti
EUR - Evropská akce
Kód UT WoS článku
000350636300016