Structural, magnetic, optical, and magneto-optical properties of CoFe2O4 thin films fabricated by a chemical approach
Identifikátory výsledku
Kód výsledku v IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F61989100%3A27240%2F19%3A10240168" target="_blank" >RIV/61989100:27240/19:10240168 - isvavai.cz</a>
Nalezeny alternativní kódy
RIV/61989100:27640/19:10240168 RIV/61989100:27710/19:10240168 RIV/61989100:27740/19:10240168 RIV/00216208:11320/19:10399567
Výsledek na webu
<a href="https://www.sciencedirect.com/science/article/pii/S0025540818314569?via%3Dihub" target="_blank" >https://www.sciencedirect.com/science/article/pii/S0025540818314569?via%3Dihub</a>
DOI - Digital Object Identifier
<a href="http://dx.doi.org/10.1016/j.materresbull.2019.05.002" target="_blank" >10.1016/j.materresbull.2019.05.002</a>
Alternativní jazyky
Jazyk výsledku
angličtina
Název v původním jazyce
Structural, magnetic, optical, and magneto-optical properties of CoFe2O4 thin films fabricated by a chemical approach
Popis výsledku v původním jazyce
Homogeneous, smooth, and partially transparent nanocrystalline thin films of CoFe2O4 were fabricated using a chemical solution approach with additional annealing for 2 h in a temperature range of 300 oC to 600 oC. Structural properties investigated by X-ray diffraction showed a single-phase spinel structure with a random crystallographic orientation for samples annealed above 400 oC. The ferromagnetic nature of prepared films was established from combined substrate with film hysteresis loops measured using a vibrating sample magnetometer. Optical and magneto-optical spectroscopic measurements revealed an improvement in the structural quality of the films after annealing up to 600 oC.
Název v anglickém jazyce
Structural, magnetic, optical, and magneto-optical properties of CoFe2O4 thin films fabricated by a chemical approach
Popis výsledku anglicky
Homogeneous, smooth, and partially transparent nanocrystalline thin films of CoFe2O4 were fabricated using a chemical solution approach with additional annealing for 2 h in a temperature range of 300 oC to 600 oC. Structural properties investigated by X-ray diffraction showed a single-phase spinel structure with a random crystallographic orientation for samples annealed above 400 oC. The ferromagnetic nature of prepared films was established from combined substrate with film hysteresis loops measured using a vibrating sample magnetometer. Optical and magneto-optical spectroscopic measurements revealed an improvement in the structural quality of the films after annealing up to 600 oC.
Klasifikace
Druh
J<sub>imp</sub> - Článek v periodiku v databázi Web of Science
CEP obor
—
OECD FORD obor
10302 - Condensed matter physics (including formerly solid state physics, supercond.)
Návaznosti výsledku
Projekt
Výsledek vznikl pri realizaci vícero projektů. Více informací v záložce Projekty.
Návaznosti
P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)
Ostatní
Rok uplatnění
2019
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů
Údaje specifické pro druh výsledku
Název periodika
Materials Research Bulletin
ISSN
0025-5408
e-ISSN
—
Svazek periodika
117
Číslo periodika v rámci svazku
September 2019
Stát vydavatele periodika
GB - Spojené království Velké Británie a Severního Irska
Počet stran výsledku
7
Strana od-do
96-102
Kód UT WoS článku
000472241200014
EID výsledku v databázi Scopus
2-s2.0-85065163975