Změny výměnné interakce a spin orbitální vazby způsobené iontovým svazkem v Co2FeSi Heuslerově slitině
Identifikátory výsledku
Kód výsledku v IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F61989100%3A27350%2F07%3A00016562" target="_blank" >RIV/61989100:27350/07:00016562 - isvavai.cz</a>
Výsledek na webu
—
DOI - Digital Object Identifier
—
Alternativní jazyky
Jazyk výsledku
angličtina
Název v původním jazyce
Ion beam induced modification of exchange interaction and spin-orbit coupling in the Co2FeSi Heusler compound
Popis výsledku v původním jazyce
A Co2FeSi ( CFS) film with L2(1) structure was irradiated with different fluences of 30 keV Ga+ ions. Structural modifications were subsequently studied using the longitudinal ( LMOKE) and quadratic ( QMOKE) magneto-optical Kerr effect. Both the coercivity and the LMOKE amplitude were found to show a similar behaviour upon irradiation: they are nearly constant up to ion fluences of approximate to 6 x 10(15) ion cm(-2), while they decrease with further increasing fluences and finally vanish at a fluenceof approximate to 9 x 10(16) ion cm(-2), when the sample becomes paramagnetic. However, contrary to this behaviour, the QMOKE signal nearly vanishes even for the smallest applied fluence of 3 x 10(14) ion cm(-2). We attribute this reduction of the QMOKEsignal to an irradiation-induced degeneration of second or higher order spin - orbit coupling, which already happens at small fluences of 30 keV Ga+ ions. On the other hand, the reduction of coercivity and LMOKE signal with high ion fluen
Název v anglickém jazyce
Ion beam induced modification of exchange interaction and spin-orbit coupling in the Co2FeSi Heusler compound
Popis výsledku anglicky
A Co2FeSi ( CFS) film with L2(1) structure was irradiated with different fluences of 30 keV Ga+ ions. Structural modifications were subsequently studied using the longitudinal ( LMOKE) and quadratic ( QMOKE) magneto-optical Kerr effect. Both the coercivity and the LMOKE amplitude were found to show a similar behaviour upon irradiation: they are nearly constant up to ion fluences of approximate to 6 x 10(15) ion cm(-2), while they decrease with further increasing fluences and finally vanish at a fluenceof approximate to 9 x 10(16) ion cm(-2), when the sample becomes paramagnetic. However, contrary to this behaviour, the QMOKE signal nearly vanishes even for the smallest applied fluence of 3 x 10(14) ion cm(-2). We attribute this reduction of the QMOKEsignal to an irradiation-induced degeneration of second or higher order spin - orbit coupling, which already happens at small fluences of 30 keV Ga+ ions. On the other hand, the reduction of coercivity and LMOKE signal with high ion fluen
Klasifikace
Druh
J<sub>x</sub> - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)
CEP obor
BM - Fyzika pevných látek a magnetismus
OECD FORD obor
—
Návaznosti výsledku
Projekt
<a href="/cs/project/GA202%2F06%2F0531" target="_blank" >GA202/06/0531: Reflexní a vlnovodné jevy v magnetických nanostrukturách</a><br>
Návaznosti
P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)
Ostatní
Rok uplatnění
2007
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů
Údaje specifické pro druh výsledku
Název periodika
Journal Phys.D: Appl.Phys.
ISSN
0022-3727
e-ISSN
—
Svazek periodika
40
Číslo periodika v rámci svazku
6
Stát vydavatele periodika
GB - Spojené království Velké Británie a Severního Irska
Počet stran výsledku
5
Strana od-do
1558-1562
Kód UT WoS článku
—
EID výsledku v databázi Scopus
—