Gigantický kvadratický magnetooptický Kerrův jev a reverzace magnetizace v Co2FeSi Heuslerových slitinách
Identifikátory výsledku
Kód výsledku v IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F61989100%3A27350%2F07%3A00016563" target="_blank" >RIV/61989100:27350/07:00016563 - isvavai.cz</a>
Výsledek na webu
—
DOI - Digital Object Identifier
—
Alternativní jazyky
Jazyk výsledku
angličtina
Název v původním jazyce
Huge quadratic magneto-optical Kerr effect and magnetization reversal in the Co2FeSi Heusler compound
Popis výsledku v původním jazyce
Co2FeSi( 1 0 0) films with L2(1) structure deposited onto MgO( 1 0 0) were studied using both the longitudinal and quadratic ( QMOKE) magneto-optical Kerr effect. The films exhibit a huge QMOKE signal with a maximum contribution of up to 30 mdeg, which is the largest QMOKE signal in reflection that has been measured thus far. This large value is a fingerprint of an exceptionally large spin - orbit coupling of second or higher order. The Co2FeSi( 1 0 0) films exhibit a rather large coercivity of 350 Oe and 70 Oe for film thicknesses of 22 nm and 98 nm, respectively. Despite the fact that the films are epitaxial, they do not provide an angular dependence of the anisotropy and the remanence in excess of 1% and 2%, respectively.
Název v anglickém jazyce
Huge quadratic magneto-optical Kerr effect and magnetization reversal in the Co2FeSi Heusler compound
Popis výsledku anglicky
Co2FeSi( 1 0 0) films with L2(1) structure deposited onto MgO( 1 0 0) were studied using both the longitudinal and quadratic ( QMOKE) magneto-optical Kerr effect. The films exhibit a huge QMOKE signal with a maximum contribution of up to 30 mdeg, which is the largest QMOKE signal in reflection that has been measured thus far. This large value is a fingerprint of an exceptionally large spin - orbit coupling of second or higher order. The Co2FeSi( 1 0 0) films exhibit a rather large coercivity of 350 Oe and 70 Oe for film thicknesses of 22 nm and 98 nm, respectively. Despite the fact that the films are epitaxial, they do not provide an angular dependence of the anisotropy and the remanence in excess of 1% and 2%, respectively.
Klasifikace
Druh
J<sub>x</sub> - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)
CEP obor
BM - Fyzika pevných látek a magnetismus
OECD FORD obor
—
Návaznosti výsledku
Projekt
<a href="/cs/project/GA202%2F06%2F0531" target="_blank" >GA202/06/0531: Reflexní a vlnovodné jevy v magnetických nanostrukturách</a><br>
Návaznosti
P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)
Ostatní
Rok uplatnění
2007
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů
Údaje specifické pro druh výsledku
Název periodika
Journal Phys.D: Appl.Phys.
ISSN
0022-3727
e-ISSN
—
Svazek periodika
40
Číslo periodika v rámci svazku
6
Stát vydavatele periodika
GB - Spojené království Velké Británie a Severního Irska
Počet stran výsledku
7
Strana od-do
1563-1569
Kód UT WoS článku
—
EID výsledku v databázi Scopus
—