Structural design of steels for brittle fracture toughness

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F61989100%3A27360%2F01%3A00001088" target="_blank" >RIV/61989100:27360/01:00001088 - isvavai.cz</a>

Výsledek na webu

—

DOI - Digital Object Identifier

—

Jazyk výsledku

angličtina

Název v původním jazyce

Structural design of steels for brittle fracture toughness

Popis výsledku v původním jazyce

This paper presents a method for quantifying probability of brittle fracture in low alloy steels. The proposed method shows how the probability of brittle fracture varies with stress intensity factor, temperature, deformation characteristics and microstructural parameters of low-alloyed steel. Application of this method on Ni-Cr steel demonstrated very good agreement of predicted temperature dependence of scatter in brittle fracture toughness with experimental results. The method enables also to calculate characteristic distance as a radial dimension from the crack tip where microcrack initiation is most probable. The characteristic distance of investigated Ni-Cr steel was found to decrease with increasing temperature. Microstructural mechanisms of initiation and propagation of brittle fracture were identified from results of fractography analysis. The proposed procedure represents a foundation for systematic control of relationship between stress-strain behaviors, toughness and reliab

Název v anglickém jazyce

Structural design of steels for brittle fracture toughness

Popis výsledku anglicky

This paper presents a method for quantifying probability of brittle fracture in low alloy steels. The proposed method shows how the probability of brittle fracture varies with stress intensity factor, temperature, deformation characteristics and microstructural parameters of low-alloyed steel. Application of this method on Ni-Cr steel demonstrated very good agreement of predicted temperature dependence of scatter in brittle fracture toughness with experimental results. The method enables also to calculate characteristic distance as a radial dimension from the crack tip where microcrack initiation is most probable. The characteristic distance of investigated Ni-Cr steel was found to decrease with increasing temperature. Microstructural mechanisms of initiation and propagation of brittle fracture were identified from results of fractography analysis. The proposed procedure represents a foundation for systematic control of relationship between stress-strain behaviors, toughness and reliab

Druh

D - Stať ve sborníku

CEP obor

JG - Hutnictví, kovové materiály

OECD FORD obor

—

Projekt

Výsledek vznikl pri realizaci vícero projektů. Více informací v záložce Projekty.

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)

Rok uplatnění

2001

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název statě ve sborníku

Transferability of fracture mechanical characteristic

ISBN

—

ISSN

—

e-ISSN

—

Počet stran výsledku

10

Strana od-do

58-68

Název nakladatele

Final project workshop - NATO SfP 972655

Místo vydání

Brno

Místo konání akce

Brno

Datum konání akce

5. 11. 2001

Typ akce podle státní příslušnosti

EUR - Evropská akce

Kód UT WoS článku

—