Probability of Brittle Fracture in Low Alloy Steels

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F61989100%3A27360%2F02%3A00006962" target="_blank" >RIV/61989100:27360/02:00006962 - isvavai.cz</a>

Výsledek na webu

—

DOI - Digital Object Identifier

—

Jazyk výsledku

angličtina

Název v původním jazyce

Probability of Brittle Fracture in Low Alloy Steels

Popis výsledku v původním jazyce

This paper presents a method for quantifying probability of brittle fracture in low alloy steels. The proposed method shows how the probability of brittle fracture varies with stress intensity factor, temperature, deformation characteristics and micro-structural parameters of low-alloyed steel. Application of this method on Ni-Cr steel demonstrated very good agreement of predicted temperature dependence of scatter in brittle fracture toughness values and with experimental results. The method enables also to calculate characteristic distance as a radial dimension from the crack tip where micro-crack initiation is most probable. The characteristic distance of investigated Ni-Cr steel was found to decrease with increasing temperature. Micro-structural mechanisms of initiation and propagation of brittle fracture were identified from results of fractography analysis. The proposed procedure represents a foundation for systematic control of relationship between stress-strain behaviors, toughn

Název v anglickém jazyce

Probability of Brittle Fracture in Low Alloy Steels

Popis výsledku anglicky

This paper presents a method for quantifying probability of brittle fracture in low alloy steels. The proposed method shows how the probability of brittle fracture varies with stress intensity factor, temperature, deformation characteristics and micro-structural parameters of low-alloyed steel. Application of this method on Ni-Cr steel demonstrated very good agreement of predicted temperature dependence of scatter in brittle fracture toughness values and with experimental results. The method enables also to calculate characteristic distance as a radial dimension from the crack tip where micro-crack initiation is most probable. The characteristic distance of investigated Ni-Cr steel was found to decrease with increasing temperature. Micro-structural mechanisms of initiation and propagation of brittle fracture were identified from results of fractography analysis. The proposed procedure represents a foundation for systematic control of relationship between stress-strain behaviors, toughn

Druh

C - Kapitola v odborné knize

CEP obor

JG - Hutnictví, kovové materiály

OECD FORD obor

—

Projekt

<a href="/cs/project/GA106%2F01%2F0342" target="_blank" >GA106/01/0342: Fyzikálně metalurgické aspekty únavového porušení konstrukčních ocelí při víceosé napjatosti cyklicky namáhaných strojních částí</a><br>

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)

Rok uplatnění

2002

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název knihy nebo sborníku

Transferability of Fracture Mechanical Characteristics

ISBN

1-4020-0795-7

Počet stran výsledku

16

Strana od-do

151-166

Počet stran knihy

—

Název nakladatele

Kluwer Academic Publishers

Místo vydání

Dordrecht

Kód UT WoS kapitoly

—