Corrosion characteristics of thermal influenced alloy 800

Popis výsledku v původním jazyce

The constitution and properties of the Cr21Ni33TiAl steel type (alloy 800) imply that this steel has a good creep, heat and corrosion resistance. It is especially for the stainless variant with a low carbon content, alloyed with titanium and aluminium for the attainment of satisfactory technological and mechanical properties. Resistance to stress corrosion in chlorides under a variety of conditions only slightly depends on carbon content and differences in chemical composition. Drop evaporation test from dilute NaCl solution reveal the deleterious effects of low-temperature sensitising of grain boundaries to intergranular corrosion, as has been documented by testing at 450 °C for 30 000 h. Heat influence lasting 30 000 h at 650 °C, which will eliminatethe susceptibility of grain boundaries to intergranular corrosion, does not impair resistance to stress corrosion cracking. Heat treatment can only little contribute to the bonding of carbon and titanium. However, this association can be

Název v anglickém jazyce

Corrosion characteristics of thermal influenced alloy 800

Popis výsledku anglicky

The constitution and properties of the Cr21Ni33TiAl steel type (alloy 800) imply that this steel has a good creep, heat and corrosion resistance. It is especially for the stainless variant with a low carbon content, alloyed with titanium and aluminium for the attainment of satisfactory technological and mechanical properties. Resistance to stress corrosion in chlorides under a variety of conditions only slightly depends on carbon content and differences in chemical composition. Drop evaporation test from dilute NaCl solution reveal the deleterious effects of low-temperature sensitising of grain boundaries to intergranular corrosion, as has been documented by testing at 450 °C for 30 000 h. Heat influence lasting 30 000 h at 650 °C, which will eliminatethe susceptibility of grain boundaries to intergranular corrosion, does not impair resistance to stress corrosion cracking. Heat treatment can only little contribute to the bonding of carbon and titanium. However, this association can be

Druh

D - Stať ve sborníku

CEP obor

JK - Koroze a povrchové úpravy materiálu

OECD FORD obor

—

Projekt

<a href="/cs/project/GA106%2F00%2F1712" target="_blank" >GA106/00/1712: Výzkum korozní odolnosti vysokolegovaných materiálů v oxidačních prostředích</a><br>

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)

Rok uplatnění

2001

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název statě ve sborníku

Eurocorr 2001

ISBN

88-85298-41-9

ISSN

—

e-ISSN

—

Počet stran výsledku

8

Strana od-do

1-8

Název nakladatele

Associazzone Italiana di Metallurgia

Místo vydání

Lake Grada

Místo konání akce

Riva del Grada, Lake Granada, Italy

Datum konání akce

30. 9. 2001

Typ akce podle státní příslušnosti

EUR - Evropská akce

Kód UT WoS článku

—