Sensitizing effect on the properties of 800 alloy

Popis výsledku v původním jazyce

On the basis of stress corrosion testing in the chloride solutions seems the 800 alloy (NiCrTiAl33-21) after solution annealing, in the comparison with other stainless steels, as very resistant against stress corrosion cracking adequately to the contentof nickel. Reducing of the content of carbon affects in this state only inexpressively its resistance. Sensitization of this material in the low critical zone of temperatures leads to increasing its sensibility to intergranular attack and stress corrosion cracking varies from transgranular to intergranular mode. These findings point out a requirement to study the changes on grain boundaries and the assurance of resistance to intergranular attack. The long-termed exposure at low temperature (e.i. 450oC-probe after 30 000h from industrial oven) leads to considerable sensibility of 800 alloy. With electrochemical potentiokinetic reactivation method (EPR-test) was reliably determine the susceptibility of this probe and the resistance on the

Název v anglickém jazyce

Sensitizing effect on the properties of 800 alloy

Popis výsledku anglicky

On the basis of stress corrosion testing in the chloride solutions seems the 800 alloy (NiCrTiAl33-21) after solution annealing, in the comparison with other stainless steels, as very resistant against stress corrosion cracking adequately to the contentof nickel. Reducing of the content of carbon affects in this state only inexpressively its resistance. Sensitization of this material in the low critical zone of temperatures leads to increasing its sensibility to intergranular attack and stress corrosion cracking varies from transgranular to intergranular mode. These findings point out a requirement to study the changes on grain boundaries and the assurance of resistance to intergranular attack. The long-termed exposure at low temperature (e.i. 450oC-probe after 30 000h from industrial oven) leads to considerable sensibility of 800 alloy. With electrochemical potentiokinetic reactivation method (EPR-test) was reliably determine the susceptibility of this probe and the resistance on the

Druh

D - Stať ve sborníku

CEP obor

JG - Hutnictví, kovové materiály

OECD FORD obor

—

Projekt

<a href="/cs/project/FT-TA%2F047" target="_blank" >FT-TA/047: Optimalizace materiálového řešení a aplikace principů protikorozní ochrany technologických zařízení a výrobků.</a><br>

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)

Rok uplatnění

2006

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název statě ve sborníku

Metal 2006, 15. mezinárodní konference metalurgie a materiálů

ISBN

80-86840-18-2

ISSN

—

e-ISSN

—

Počet stran výsledku

5

Strana od-do

18-22

Název nakladatele

Tanger, s.r.o., ve spolupráci MARQ,

Místo vydání

Ostrava 10,

Místo konání akce

—

Datum konání akce

—

Typ akce podle státní příslušnosti

—

Kód UT WoS článku

—