DAMAGE OF ALLOY 800 AFTER LOW TEMPERATURE SENSITIZATION
Identifikátory výsledku
Kód výsledku v IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F61989100%3A27360%2F08%3A00019452" target="_blank" >RIV/61989100:27360/08:00019452 - isvavai.cz</a>
Výsledek na webu
—
DOI - Digital Object Identifier
—
Alternativní jazyky
Jazyk výsledku
angličtina
Název v původním jazyce
DAMAGE OF ALLOY 800 AFTER LOW TEMPERATURE SENSITIZATION
Popis výsledku v původním jazyce
Failure of the Alloy 800 (Cr21Ni33TiAl), exposed in chemical industrial furnace to the temperature range from 450 up to 650°C, became on the lower temperature part. Two methods ? Electrochemical potentiokinetic reactivation test (EPR) and drop evaporation test (DET) reveal the deleterious effect of lower temperature and confirm low temperature sensitization of Alloy 800 after 30000 hours working time. These results are in agreement with measured concentration profiles of Cr at grain boundaries as well as stress corrosion cracking tests in MgCl2 solution. Polarization curves of carbides and intermetallic phases that influence intergranular corrosion and cracking of Alloy 800 were also compared and discussed.
Název v anglickém jazyce
DAMAGE OF ALLOY 800 AFTER LOW TEMPERATURE SENSITIZATION
Popis výsledku anglicky
Failure of the Alloy 800 (Cr21Ni33TiAl), exposed in chemical industrial furnace to the temperature range from 450 up to 650°C, became on the lower temperature part. Two methods ? Electrochemical potentiokinetic reactivation test (EPR) and drop evaporation test (DET) reveal the deleterious effect of lower temperature and confirm low temperature sensitization of Alloy 800 after 30000 hours working time. These results are in agreement with measured concentration profiles of Cr at grain boundaries as well as stress corrosion cracking tests in MgCl2 solution. Polarization curves of carbides and intermetallic phases that influence intergranular corrosion and cracking of Alloy 800 were also compared and discussed.
Klasifikace
Druh
D - Stať ve sborníku
CEP obor
JK - Koroze a povrchové úpravy materiálu
OECD FORD obor
—
Návaznosti výsledku
Projekt
<a href="/cs/project/GA106%2F06%2F1621" target="_blank" >GA106/06/1621: Korozní odolnost pasivního stavu vysokolegovaných materiálů</a><br>
Návaznosti
P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)
Ostatní
Rok uplatnění
2008
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů
Údaje specifické pro druh výsledku
Název statě ve sborníku
New Methods of Damage and Failure Analysis of Structural Parts
ISBN
978-80-248-1813-9
ISSN
—
e-ISSN
—
Počet stran výsledku
8
Strana od-do
—
Název nakladatele
VŠB TU Ostrava
Místo vydání
Ostrava
Místo konání akce
Ostrava
Datum konání akce
8. 9. 2008
Typ akce podle státní příslušnosti
WRD - Celosvětová akce
Kód UT WoS článku
—