Forming and technological processing of single crystals on the base of tungsten and molybdenum

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F61989100%3A27360%2F02%3A00001691" target="_blank" >RIV/61989100:27360/02:00001691 - isvavai.cz</a>

Výsledek na webu

—

DOI - Digital Object Identifier

—

Jazyk výsledku

angličtina

Název v původním jazyce

Forming and technological processing of single crystals on the base of tungsten and molybdenum

Popis výsledku v původním jazyce

The aim of this work was to assess the rhenium and iridium influence on structural and mechanical characteristics at forming single crystals of high-melting metals. Low-alloyed alloys of W and Mo doped with Ir and Re, the initial length about 204 mm anddiameters 11 and 13 mm, were prepared by the plasma metallurgy. The conditions of forming single crystals on the base of tungsten consisted of a specimen heating in the furnace in the atmosphere of hydrogen to the temperature of 1450 °C followed by rotary swaging the result of which were rods of the diameter about 5.5 mm and continuous forging to the final diameter about 4 mm. The final reduction to the diameter 0.5 mm was performed by means of the drum drawing.

Název v anglickém jazyce

Forming and technological processing of single crystals on the base of tungsten and molybdenum

Popis výsledku anglicky

The aim of this work was to assess the rhenium and iridium influence on structural and mechanical characteristics at forming single crystals of high-melting metals. Low-alloyed alloys of W and Mo doped with Ir and Re, the initial length about 204 mm anddiameters 11 and 13 mm, were prepared by the plasma metallurgy. The conditions of forming single crystals on the base of tungsten consisted of a specimen heating in the furnace in the atmosphere of hydrogen to the temperature of 1450 °C followed by rotary swaging the result of which were rods of the diameter about 5.5 mm and continuous forging to the final diameter about 4 mm. The final reduction to the diameter 0.5 mm was performed by means of the drum drawing.

Druh

D - Stať ve sborníku

CEP obor

JG - Hutnictví, kovové materiály

OECD FORD obor

—

Projekt

<a href="/cs/project/GA106%2F99%2F0824" target="_blank" >GA106/99/0824: Strukturně definované materiály vysokotavitelných kovů pro aplikace v elektrotechnice a vakuové technice</a><br>

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)

Rok uplatnění

2002

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název statě ve sborníku

Development of Materials Science in Research and Education

ISBN

80-85912-85-8

ISSN

—

e-ISSN

—

Počet stran výsledku

2

Strana od-do

17-18

Název nakladatele

MAXDORF, s.r.o.

Místo vydání

Praha

Místo konání akce

Ostravice

Datum konání akce

10. 9. 2002

Typ akce podle státní příslušnosti

WRD - Celosvětová akce

Kód UT WoS článku

—