The influence of technological processing on structural characteristics of tungsten and molybdenum single crystals

Popis výsledku v původním jazyce

Low-alloyed alloys of W and Mo doped with Ir and Re were prepared by the plasma metallurgy. The plasma heating was used for intensification of metallurgical processes and allows obtaining of single crystals with large diameters and low carbon content. Technological processing of single crystals was performed in Rotumo, s.r.o. in Rožnov pod Radhoštěm according to a standard procedure applied in the case of polycrystalline materials. Wires of the diameter about 4 mm and 0,5 mm were prepared. The aim of this work was to assess the rhenium and iridium influence on structural characteristics at forming of these single crystals. On the basis of X-ray analysis and metallographic study was evaluated the possibility of the obtaining of single crystal structureafter recrystallization annealing.

Název v anglickém jazyce

The influence of technological processing on structural characteristics of tungsten and molybdenum single crystals

Popis výsledku anglicky

Low-alloyed alloys of W and Mo doped with Ir and Re were prepared by the plasma metallurgy. The plasma heating was used for intensification of metallurgical processes and allows obtaining of single crystals with large diameters and low carbon content. Technological processing of single crystals was performed in Rotumo, s.r.o. in Rožnov pod Radhoštěm according to a standard procedure applied in the case of polycrystalline materials. Wires of the diameter about 4 mm and 0,5 mm were prepared. The aim of this work was to assess the rhenium and iridium influence on structural characteristics at forming of these single crystals. On the basis of X-ray analysis and metallographic study was evaluated the possibility of the obtaining of single crystal structureafter recrystallization annealing.

Druh

D - Stať ve sborníku

CEP obor

JG - Hutnictví, kovové materiály

OECD FORD obor

—

Projekt

<a href="/cs/project/GA106%2F03%2F0048" target="_blank" >GA106/03/0048: Materiály na bázi vysoce čistých monokrystalů vysokotavitelných kovů pro funkční prvky elektro-vakuových a kontrolně-měřicích přístrojů</a><br>

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)

Rok uplatnění

2004

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název statě ve sborníku

Acta Metallurgica Slovaca

ISBN

1335-1532

ISSN

—

e-ISSN

—

Počet stran výsledku

4

Strana od-do

870-873

Název nakladatele

Hutnická fakulta Technické univerzity Košice

Místo vydání

Košice

Místo konání akce

Stará Lesná

Datum konání akce

28. 4. 2004

Typ akce podle státní příslušnosti

EUR - Evropská akce

Kód UT WoS článku

—