The influence of cooling conditions on the structure and properties of hot rolled dual phase steel

Kód výsledku v IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F61989100%3A27360%2F02%3A00001739" target="_blank" >RIV/61989100:27360/02:00001739 - isvavai.cz</a>
Výsledek na webu
—
DOI - Digital Object Identifier
—

Jazyk výsledku
angličtina
Název v původním jazyce
The influence of cooling conditions on the structure and properties of hot rolled dual phase steel
Popis výsledku v původním jazyce
The effect of different cooling patterns after hot rolling on the mechanical properties and structure formation of 0.05% C - 0.83% Mn - 1.13% Si - 0.53% Cr - 0.33% Mo steel is established in this work. Optimum results, with a Tensile Strength of 595 MPa,Proof Stress/Tensile Strength ratio of 0.62 and elongation of 30.2 %, have been obtained after cooling down from finished temperature of 880 °C to a coiling temperature of 550 °C with a cooling rate of 30 °C/s.
Název v anglickém jazyce
The influence of cooling conditions on the structure and properties of hot rolled dual phase steel
Popis výsledku anglicky
The effect of different cooling patterns after hot rolling on the mechanical properties and structure formation of 0.05% C - 0.83% Mn - 1.13% Si - 0.53% Cr - 0.33% Mo steel is established in this work. Optimum results, with a Tensile Strength of 595 MPa,Proof Stress/Tensile Strength ratio of 0.62 and elongation of 30.2 %, have been obtained after cooling down from finished temperature of 880 °C to a coiling temperature of 550 °C with a cooling rate of 30 °C/s.

Projekt
<a href="/cs/project/GA106%2F01%2F0371" target="_blank" >GA106/01/0371: Strukturní aspekty přímého válcování tenkých ocelových bram</a><br>
Návaznosti
P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)

Rok uplatnění
2002
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Podobné výsledky(10)