Analysis of Billet´S Pipe Mould Temperature Field of CCM No. 3 in ISPAT NOVÁ HUŤ a. s.

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F61989100%3A27360%2F03%3A00008609" target="_blank" >RIV/61989100:27360/03:00008609 - isvavai.cz</a>

Výsledek na webu

—

DOI - Digital Object Identifier

—

Jazyk výsledku

angličtina

Název v původním jazyce

Analysis of Billet´S Pipe Mould Temperature Field of CCM No. 3 in ISPAT NOVÁ HUŤ a. s.

Popis výsledku v původním jazyce

Six-stream CCM No. 3, supplied by the CONCAST STANDARD, was started in run in ISPAT NOVÁ HUŤ a.s. in 1999. It casts quadrate billets 115 mm, 160 mm and small slab 102x160 mm. Tube mould of this casting machine need to be untimely discarded from the reason of work security, because their lifetime is diminished with deep longitudinal grooves in the region of meniscus. The emergence of grooves relates not with the number of heats cast on the mould. This problem was consulted with the supplier of the CCM, some remedies were proved, but in spite of that the problem was till now not satisfactory completely solved. On of possible causes could be the enhanced temperatures of copper wall, which exceeds the temperature of recrystallization and so decreases the mould hardness and subsequently causes the formation of grooves. Not only for the reason of verifying this presumption the measurement of the effects of selected technological parameters changes of casting on the temperature of copper wall

Název v anglickém jazyce

Analysis of Billet´S Pipe Mould Temperature Field of CCM No. 3 in ISPAT NOVÁ HUŤ a. s.

Popis výsledku anglicky

Six-stream CCM No. 3, supplied by the CONCAST STANDARD, was started in run in ISPAT NOVÁ HUŤ a.s. in 1999. It casts quadrate billets 115 mm, 160 mm and small slab 102x160 mm. Tube mould of this casting machine need to be untimely discarded from the reason of work security, because their lifetime is diminished with deep longitudinal grooves in the region of meniscus. The emergence of grooves relates not with the number of heats cast on the mould. This problem was consulted with the supplier of the CCM, some remedies were proved, but in spite of that the problem was till now not satisfactory completely solved. On of possible causes could be the enhanced temperatures of copper wall, which exceeds the temperature of recrystallization and so decreases the mould hardness and subsequently causes the formation of grooves. Not only for the reason of verifying this presumption the measurement of the effects of selected technological parameters changes of casting on the temperature of copper wall

Druh

D - Stať ve sborníku

CEP obor

JG - Hutnictví, kovové materiály

OECD FORD obor

—

Projekt

Výsledek vznikl pri realizaci vícero projektů. Více informací v záložce Projekty.

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)

Rok uplatnění

2003

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název statě ve sborníku

Proceedings 5th International Metallurgical Conference on Continuous Casting of Billets and Modelling of Steelmaking Processes

ISBN

80-239-0861-8

ISSN

—

e-ISSN

—

Počet stran výsledku

10

Strana od-do

126-135

Název nakladatele

Třinecké železárny, a. s.

Místo vydání

Třinec

Místo konání akce

Třinec

Datum konání akce

21. 10. 2003

Typ akce podle státní příslušnosti

EUR - Evropská akce

Kód UT WoS článku

—