Hodnocení vlivu množství zbytkového austenitu a velikosti feritického zrna na mechanické vlastnosti trip ocelí

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F61989100%3A27360%2F04%3A00010853" target="_blank" >RIV/61989100:27360/04:00010853 - isvavai.cz</a>

Výsledek na webu

—

DOI - Digital Object Identifier

—

Jazyk výsledku

angličtina

Název v původním jazyce

Hodnocení vlivu množství zbytkového austenitu a velikosti feritického zrna na mechanické vlastnosti trip ocelí

Popis výsledku v původním jazyce

High strength steels with good formability are used for weight reduction in automobile industry especially. TRIP steels are one of these groups of high strength steels. Properties of TRIP steels, like tensile strength to 1200 MPa and elongation to 35%, make them promising for further replacement of common low carbon steels. Microstructure of TRIP steels is attractive cause it is made up by multiphase structure of polygonal ferrite, pearlite, bainite, acicular ferrite and certain amount of retained austenite. In consequence of TRIP effect processing during subsequent cold forming retained austenite increases strength to ductility balance. Mechanical properties of TRIP steels are strongly affected by retained austenite volume fraction and stability.In this work the influences of retained austenite volume fraction and ferritic grain size on mechanical properties are elaborated. The specific shape samples are rolled for this reason. Through this specific sample shape it is attained combina

Název v anglickém jazyce

Hodnocení vlivu množství zbytkového austenitu a velikosti feritického zrna na mechanické vlastnosti trip ocelí

Popis výsledku anglicky

High strength steels with good formability are used for weight reduction in automobile industry especially. TRIP steels are one of these groups of high strength steels. Properties of TRIP steels, like tensile strength to 1200 MPa and elongation to 35%, make them promising for further replacement of common low carbon steels. Microstructure of TRIP steels is attractive cause it is made up by multiphase structure of polygonal ferrite, pearlite, bainite, acicular ferrite and certain amount of retained austenite. In consequence of TRIP effect processing during subsequent cold forming retained austenite increases strength to ductility balance. Mechanical properties of TRIP steels are strongly affected by retained austenite volume fraction and stability.In this work the influences of retained austenite volume fraction and ferritic grain size on mechanical properties are elaborated. The specific shape samples are rolled for this reason. Through this specific sample shape it is attained combina

Druh

D - Stať ve sborníku

CEP obor

JG - Hutnictví, kovové materiály

OECD FORD obor

—

Projekt

<a href="/cs/project/GA106%2F04%2F0601" target="_blank" >GA106/04/0601: Využití transformačně indukované plasticity (TRIP) u technologií tváření oceli</a><br>

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)

Rok uplatnění

2004

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název statě ve sborníku

18. Mezinárodní sympozium Struktura a vlastnosti konstrukčních materiálů a výrobků

ISBN

1429-6065

ISSN

—

e-ISSN

—

Počet stran výsledku

6

Strana od-do

141-146

Název nakladatele

Politechnika Opolska

Místo vydání

Opole

Místo konání akce

Rožnov pod Radhoštěm

Datum konání akce

30. 12. 2004

Typ akce podle státní příslušnosti

EUR - Evropská akce

Kód UT WoS článku

—