Vliv deformace za tepla na množství zbytkového austenitu v TRIP oceli

Popis výsledku v původním jazyce

High strength steels with good formability are used for weight reduction in automobile industry especially. TRIP steels are one of these groups of high strength steels. Properties of TRIP steels, like tensile strength to 1200 MPa and elongation to 35%, make them promising for further replacement of common low carbon steels. Microstructure of TRIP steels is attractive cause it is made up by multiphase structure of polygonal ferrite, pearlite, bainite, acicular ferrite and certain amount of retained austenite. In consequence of TRIP effect processing during subsequent cold forming retained austenite increases strength to ductility balance. Mechanical properties of TRIP steels are strongly affected by retained austenite volume fraction and stability.In this work the influence of hot deformation on retained austenite volume fraction in C-Mn-Si TRIP steel is elaborated. This influence is presented different way in various literature sources. This is caused probably by strong affection of re

Název v anglickém jazyce

Vliv deformace za tepla na množství zbytkového austenitu v TRIP oceli

Popis výsledku anglicky

High strength steels with good formability are used for weight reduction in automobile industry especially. TRIP steels are one of these groups of high strength steels. Properties of TRIP steels, like tensile strength to 1200 MPa and elongation to 35%, make them promising for further replacement of common low carbon steels. Microstructure of TRIP steels is attractive cause it is made up by multiphase structure of polygonal ferrite, pearlite, bainite, acicular ferrite and certain amount of retained austenite. In consequence of TRIP effect processing during subsequent cold forming retained austenite increases strength to ductility balance. Mechanical properties of TRIP steels are strongly affected by retained austenite volume fraction and stability.In this work the influence of hot deformation on retained austenite volume fraction in C-Mn-Si TRIP steel is elaborated. This influence is presented different way in various literature sources. This is caused probably by strong affection of re

Druh

D - Stať ve sborníku

CEP obor

JG - Hutnictví, kovové materiály

OECD FORD obor

—

Projekt

<a href="/cs/project/GA106%2F04%2F0601" target="_blank" >GA106/04/0601: Využití transformačně indukované plasticity (TRIP) u technologií tváření oceli</a><br>

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)

Rok uplatnění

2004

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název statě ve sborníku

Sborník mezinárodní vědecké konference FORMING 2004

ISBN

80-227-2091-7

ISSN

—

e-ISSN

—

Počet stran výsledku

6

Strana od-do

326-331

Název nakladatele

Slovenská technická univerzita v Bratislave

Místo vydání

Bratislava

Místo konání akce

Štrbské Pleso, Slovensko

Datum konání akce

9. 9. 2004

Typ akce podle státní příslušnosti

EUR - Evropská akce

Kód UT WoS článku

—