Posouzení uplatnění nových technologických postupů válcování blokových předlitků do bloků s cílem zhutnění jejich středové zóny

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F61989100%3A27360%2F05%3A00012930" target="_blank" >RIV/61989100:27360/05:00012930 - isvavai.cz</a>

Výsledek na webu

—

DOI - Digital Object Identifier

—

Jazyk výsledku

angličtina

Název v původním jazyce

Assessment of new rolling process of continuously cast sections into blooms with enhanced strain penetration

Popis výsledku v původním jazyce

This paper presents investigation of causes of cracking in the interior of thick rolled products. The process comprised rolling of continuously cast sections of initial 525 mm diameter from 42CrMo4 steel in the blooming mill of the Třinecké Železárny steelworks into blooms of 285 by 285 mm dimensions. First part of the study concerns research into possible causes of cracking with respect to thermal conditions of rolling and microstructural features of steel. Examination of microstructure revealed casting cracks on prior austenite grain boundaries, which might initiate formation of the critical cracks. Second part of paper contains FormFEM program simulation-aided feasibility study of enhancing the amount of reduction in the bloom centre by means of bloom surface undercooling. Surface undercooling should be achieved by extending the delay prior to bloom's entering the rolling mill. Comparison of common rolling process and the newly-designed process is provided. Primary attention has bee

Název v anglickém jazyce

Assessment of new rolling process of continuously cast sections into blooms with enhanced strain penetration

Popis výsledku anglicky

This paper presents investigation of causes of cracking in the interior of thick rolled products. The process comprised rolling of continuously cast sections of initial 525 mm diameter from 42CrMo4 steel in the blooming mill of the Třinecké Železárny steelworks into blooms of 285 by 285 mm dimensions. First part of the study concerns research into possible causes of cracking with respect to thermal conditions of rolling and microstructural features of steel. Examination of microstructure revealed casting cracks on prior austenite grain boundaries, which might initiate formation of the critical cracks. Second part of paper contains FormFEM program simulation-aided feasibility study of enhancing the amount of reduction in the bloom centre by means of bloom surface undercooling. Surface undercooling should be achieved by extending the delay prior to bloom's entering the rolling mill. Comparison of common rolling process and the newly-designed process is provided. Primary attention has bee

Druh

J_x - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)

CEP obor

JG - Hutnictví, kovové materiály

OECD FORD obor

—

Projekt

<a href="/cs/project/GA106%2F04%2F1452" target="_blank" >GA106/04/1452: RollFem 3D</a><br>

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)

Rok uplatnění

2005

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

Acta Metallurgica Slovaca

ISSN

1335-1532

e-ISSN

—

Svazek periodika

11

Číslo periodika v rámci svazku

2

Stát vydavatele periodika

SK - Slovenská republika

Počet stran výsledku

6

Strana od-do

226-231

Kód UT WoS článku

—

EID výsledku v databázi Scopus

—