Vliv podchlazení povrchových vrstev PLP na distribuci deformace do jádra při válcování za tepla

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F61989100%3A27360%2F06%3A00014242" target="_blank" >RIV/61989100:27360/06:00014242 - isvavai.cz</a>

Výsledek na webu

—

DOI - Digital Object Identifier

—

Jazyk výsledku

angličtina

Název v původním jazyce

Influence of Undercooled Surface of CCSP on Core Distribution of Longitudinal and Transversal Stresses During Hot Rolling

Popis výsledku v původním jazyce

Investigation of causes of cracking in the interior of thick rolled products. First part of the study concerns research into possible causes of cracking with respect to thermal conditions of rolling and microstructural features of steel. Examination of microstructure revealed casting cracks on prior austenite grain boundaries, which might initiate formation of the critical cracks. Second part of paper contains FormFEM and Forge2005 program simulation-aided feasibility study of enhancing the amount of reduction in the bloom centre by means of bloom surface undercooling. Comparison of common rolling process and the newly-designed process is provided. Primary attention has been paid to the magnitude (and sign) of the longitudinal and transversal stressesin the bloom cross-section and to penetration of strain into the bloom centre.

Název v anglickém jazyce

Influence of Undercooled Surface of CCSP on Core Distribution of Longitudinal and Transversal Stresses During Hot Rolling

Popis výsledku anglicky

Investigation of causes of cracking in the interior of thick rolled products. First part of the study concerns research into possible causes of cracking with respect to thermal conditions of rolling and microstructural features of steel. Examination of microstructure revealed casting cracks on prior austenite grain boundaries, which might initiate formation of the critical cracks. Second part of paper contains FormFEM and Forge2005 program simulation-aided feasibility study of enhancing the amount of reduction in the bloom centre by means of bloom surface undercooling. Comparison of common rolling process and the newly-designed process is provided. Primary attention has been paid to the magnitude (and sign) of the longitudinal and transversal stressesin the bloom cross-section and to penetration of strain into the bloom centre.

Druh

J_x - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)

CEP obor

JG - Hutnictví, kovové materiály

OECD FORD obor

—

Projekt

<a href="/cs/project/FI-IM2%2F043" target="_blank" >FI-IM2/043: *Nové progresivní technologické postupy výroby ocelových výrobků.</a><br>

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)

Rok uplatnění

2006

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

Metalurgija

ISSN

0543-5846

e-ISSN

—

Svazek periodika

45

Číslo periodika v rámci svazku

3

Stát vydavatele periodika

HR - Chorvatská republika

Počet stran výsledku

1

Strana od-do

248-248

Kód UT WoS článku

—

EID výsledku v databázi Scopus

—