The influence of adding CaCN2 on the SBQ steel metallographic cleanness

Popis výsledku v původním jazyce

The steel with control sulphur content, SBQ steel, is characterized by increased sulphur content and therefore it must be made by special technology preventing sulphur removal. Its continuous casting can fetch along many technical problems, mainly the nozzle clogging during continuous casting operations. It is caused by the sticking of the inclusions on the nozzles sides. The worst inclusions are inclusions type Al2O3 and CaS. Because of this reason it is necessary to modify the Al2O3 inclusions on theliquid aluminates and prevent the genesis of the CaS inclusions in the liquid steel. There were done test heats and were subscribed the exhibits of the chosen steel grade with the aim to review the modification of the Al2O3 inclusions with the help of nitrogenous lime CaCN2 in the grant project No. 106/04/0029.

Název v anglickém jazyce

The influence of adding CaCN2 on the SBQ steel metallographic cleanness

Popis výsledku anglicky

The steel with control sulphur content, SBQ steel, is characterized by increased sulphur content and therefore it must be made by special technology preventing sulphur removal. Its continuous casting can fetch along many technical problems, mainly the nozzle clogging during continuous casting operations. It is caused by the sticking of the inclusions on the nozzles sides. The worst inclusions are inclusions type Al2O3 and CaS. Because of this reason it is necessary to modify the Al2O3 inclusions on theliquid aluminates and prevent the genesis of the CaS inclusions in the liquid steel. There were done test heats and were subscribed the exhibits of the chosen steel grade with the aim to review the modification of the Al2O3 inclusions with the help of nitrogenous lime CaCN2 in the grant project No. 106/04/0029.

Druh

D - Stať ve sborníku

CEP obor

JG - Hutnictví, kovové materiály

OECD FORD obor

—

Projekt

<a href="/cs/project/GA106%2F04%2F0029" target="_blank" >GA106/04/0029: Řízení vlastností tekuté oceli před jejím plynulým odléváním s cílem minimalizovat vady předlitku</a><br>

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)

Rok uplatnění

2005

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název statě ve sborníku

Den interních doktorandů 2005

ISBN

80-248-0978-8

ISSN

—

e-ISSN

—

Počet stran výsledku

2

Strana od-do

6-7

Název nakladatele

VŠB - Technická univerzita Ostrava

Místo vydání

Ostrava

Místo konání akce

Ostrava-Poruba

Datum konání akce

12. 12. 2005

Typ akce podle státní příslušnosti

CST - Celostátní akce

Kód UT WoS článku

—