Statistický rozbor vlivu vybraných parametrů na zarůstání výlevek mezipánve při odlévání SBQ ocelí

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F61989100%3A27360%2F06%3A00014197" target="_blank" >RIV/61989100:27360/06:00014197 - isvavai.cz</a>

Výsledek na webu

—

DOI - Digital Object Identifier

—

Jazyk výsledku

angličtina

Název v původním jazyce

Statistical Analysis of the Chosen Parameters Influence on the Nozzle Clogging in Tundish at SBQ Steel Continuous Casting

Popis výsledku v původním jazyce

The steel with control sulphur content, SBQ steel, is characterized by increased sulphur content and therefore it must be made by special technology preventing sulphur removal. The steel is cast on the continuous casting machine after the ending of secondary metallurgy procedures. It can fetch along many technical problems, mainly the nozzle clogging during continuous casting operations. It is caused by the sticking of the inclusions on the nozzles sides. The worst inclusions are inclusions type Al2O3 and CaS. Because of this reason it is necessary to modify the Al2O3 inclusions on the liquid aluminates and prevent the genesis of the CaS inclusions in the liquid steel. As the modifier it is used mainly calcium in various form, in most cases in form CaSi. Sometimes it is used calcium in form CaCN2 (nitrogenous lime) because some types of SBQ steel contains enhanced nitrogen content. There were done the statistical analyze of the chosen 90 heats SBQ steel with the aim to determine the in

Název v anglickém jazyce

Statistical Analysis of the Chosen Parameters Influence on the Nozzle Clogging in Tundish at SBQ Steel Continuous Casting

Popis výsledku anglicky

The steel with control sulphur content, SBQ steel, is characterized by increased sulphur content and therefore it must be made by special technology preventing sulphur removal. The steel is cast on the continuous casting machine after the ending of secondary metallurgy procedures. It can fetch along many technical problems, mainly the nozzle clogging during continuous casting operations. It is caused by the sticking of the inclusions on the nozzles sides. The worst inclusions are inclusions type Al2O3 and CaS. Because of this reason it is necessary to modify the Al2O3 inclusions on the liquid aluminates and prevent the genesis of the CaS inclusions in the liquid steel. As the modifier it is used mainly calcium in various form, in most cases in form CaSi. Sometimes it is used calcium in form CaCN2 (nitrogenous lime) because some types of SBQ steel contains enhanced nitrogen content. There were done the statistical analyze of the chosen 90 heats SBQ steel with the aim to determine the in

Druh

D - Stať ve sborníku

CEP obor

JG - Hutnictví, kovové materiály

OECD FORD obor

—

Projekt

<a href="/cs/project/GA106%2F04%2F0029" target="_blank" >GA106/04/0029: Řízení vlastností tekuté oceli před jejím plynulým odléváním s cílem minimalizovat vady předlitku</a><br>

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)

Rok uplatnění

2006

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název statě ve sborníku

13. Internationaler Studententag der Metallurgie

ISBN

3-901384-18-9

ISSN

—

e-ISSN

—

Počet stran výsledku

8

Strana od-do

128-135

Název nakladatele

ASMET, Austrian Society for Metallurgy and Materials

Místo vydání

Leoben

Místo konání akce

—

Datum konání akce

—

Typ akce podle státní příslušnosti

—

Kód UT WoS článku

—