Specifika přípravy Ni-Ti paměťových slitin

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F61989100%3A27360%2F06%3A00014190" target="_blank" >RIV/61989100:27360/06:00014190 - isvavai.cz</a>

Výsledek na webu

—

DOI - Digital Object Identifier

—

Jazyk výsledku

angličtina

Název v původním jazyce

Specifications of preparation of Ni-Ti shape memory alloys

Popis výsledku v původním jazyce

Intermetallic compound containing approx. 50 at.% Ni and 50 at. % Ti is considered as standard shape memory alloy. The basic requirement to metallurgy of these advanced materials is strict adherence to chemical composition of the alloy, which is the maincondition for obtaining of the alloy with the required transformation temperatures. At use plasma melting, material is placed into copper water-cooled mold. For the melting as such it is necessary to use the cleanest available argon due to high affinityof titanium to oxygen. Plasma temperature achieves at this method of melting 6500 K. Chemical homogeneity can be achieved at vacuum induction melting. Material of crucible has at this method the principal influence on quality of ingot. Ni-Ti based alloys are usually melted at the temperature of approx. 1500 °C. For obtaining of wire it is best to use technology of swagging in combination with subsequent drawing. This article deals with preparation of Ni-Ti shape memory alloys in plasma

Název v anglickém jazyce

Specifications of preparation of Ni-Ti shape memory alloys

Popis výsledku anglicky

Intermetallic compound containing approx. 50 at.% Ni and 50 at. % Ti is considered as standard shape memory alloy. The basic requirement to metallurgy of these advanced materials is strict adherence to chemical composition of the alloy, which is the maincondition for obtaining of the alloy with the required transformation temperatures. At use plasma melting, material is placed into copper water-cooled mold. For the melting as such it is necessary to use the cleanest available argon due to high affinityof titanium to oxygen. Plasma temperature achieves at this method of melting 6500 K. Chemical homogeneity can be achieved at vacuum induction melting. Material of crucible has at this method the principal influence on quality of ingot. Ni-Ti based alloys are usually melted at the temperature of approx. 1500 °C. For obtaining of wire it is best to use technology of swagging in combination with subsequent drawing. This article deals with preparation of Ni-Ti shape memory alloys in plasma

Druh

D - Stať ve sborníku

CEP obor

JG - Hutnictví, kovové materiály

OECD FORD obor

—

Projekt

<a href="/cs/project/GA106%2F03%2F0231" target="_blank" >GA106/03/0231: Vliv procesu přípravy paměťových materiálů Ni-Ti-Me na jejich strukturu a možnosti řízení jejich transformačních charakteristik</a><br>

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)

Rok uplatnění

2006

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název statě ve sborníku

13. Internationaler Studententag der Metallurgie

ISBN

3-901384-18-9

ISSN

—

e-ISSN

—

Počet stran výsledku

10

Strana od-do

196-2005

Název nakladatele

ASMET, Austrian Society for Metallurgy and Materials

Místo vydání

Leoben

Místo konání akce

—

Datum konání akce

—

Typ akce podle státní příslušnosti

—

Kód UT WoS článku

—