Influence of conditions of preparation on structural characteristics of Ni-Ti alloys

Popis výsledku v původním jazyce

Intermetallic compound containing approx. 50 at.% Ni and 50 at. % Ti is considered as standard shape memory alloy. The basic requirement to metallurgy of these advanced materials is strict adherence to chemical composition of the alloy, which is the maincondition for obtaining of the alloy with the required transformation temperatures. At use plasma melting, material is placed into copper water-cooled mold. This is drifted by bolt under plasma burner. Argon is used as plasma forming gas. For the melting as such it is necessary to use the cleanest available argon due to high affinity of titanium to oxygen. Plasma temperature achieves at this method of melting 6500 K. Chemical homogeneity can be achieved at vacuum induction melting. Material of cruciblehas at this method the principal influence on quality of ingot. Crucibles made of Al2O3 and MgO cannot be used due to oxygen content. Oxygen contained in graphite crucible can be neglected, it is, however, necessary to take into account

Název v anglickém jazyce

Influence of conditions of preparation on structural characteristics of Ni-Ti alloys

Popis výsledku anglicky

Intermetallic compound containing approx. 50 at.% Ni and 50 at. % Ti is considered as standard shape memory alloy. The basic requirement to metallurgy of these advanced materials is strict adherence to chemical composition of the alloy, which is the maincondition for obtaining of the alloy with the required transformation temperatures. At use plasma melting, material is placed into copper water-cooled mold. This is drifted by bolt under plasma burner. Argon is used as plasma forming gas. For the melting as such it is necessary to use the cleanest available argon due to high affinity of titanium to oxygen. Plasma temperature achieves at this method of melting 6500 K. Chemical homogeneity can be achieved at vacuum induction melting. Material of cruciblehas at this method the principal influence on quality of ingot. Crucibles made of Al2O3 and MgO cannot be used due to oxygen content. Oxygen contained in graphite crucible can be neglected, it is, however, necessary to take into account

Druh

J_x - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)

CEP obor

JG - Hutnictví, kovové materiály

OECD FORD obor

—

Projekt

<a href="/cs/project/GA106%2F03%2F0231" target="_blank" >GA106/03/0231: Vliv procesu přípravy paměťových materiálů Ni-Ti-Me na jejich strukturu a možnosti řízení jejich transformačních charakteristik</a><br>

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)

Rok uplatnění

2005

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

Acta Metallurgica Slovaca

ISSN

1335-1532

e-ISSN

—

Svazek periodika

11

Číslo periodika v rámci svazku

3

Stát vydavatele periodika

SK - Slovenská republika

Počet stran výsledku

9

Strana od-do

284-292

Kód UT WoS článku

—

EID výsledku v databázi Scopus

—