Effect of cold rolling and annealing conditions on mechanical properties of HSLA steel strips

Popis výsledku v původním jazyce

A large testing programme of a strip steel grade, microalloyed by vanadium, titanium and niobium, was conducted. The experiment was based on combination of cold rolling, recrystallization annealing, mechanical testing (hardness test, tensile test) and metallographic examinations. Samples of thickness 3.9 mm, which were taken from the hot rolled strip, underwent a total reduction in the range from 5 % to 75 % in the laboratory rolling mill. Afterwards the laboratory mill products were annealed in the vacuum furnace with the protective gas atmosphere consisting of N2+H2. Hardness HB, elongation, yield stress, tensile strength and ratio of yield stress to tensile strength were determined during testing the annealed samples.

Název v anglickém jazyce

Effect of cold rolling and annealing conditions on mechanical properties of HSLA steel strips

Popis výsledku anglicky

A large testing programme of a strip steel grade, microalloyed by vanadium, titanium and niobium, was conducted. The experiment was based on combination of cold rolling, recrystallization annealing, mechanical testing (hardness test, tensile test) and metallographic examinations. Samples of thickness 3.9 mm, which were taken from the hot rolled strip, underwent a total reduction in the range from 5 % to 75 % in the laboratory rolling mill. Afterwards the laboratory mill products were annealed in the vacuum furnace with the protective gas atmosphere consisting of N2+H2. Hardness HB, elongation, yield stress, tensile strength and ratio of yield stress to tensile strength were determined during testing the annealed samples.

Druh

D - Stať ve sborníku

CEP obor

JG - Hutnictví, kovové materiály

OECD FORD obor

—

Projekt

—

Návaznosti

Z - Vyzkumny zamer (s odkazem do CEZ)

Rok uplatnění

2006

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název statě ve sborníku

13. mezinárodní knference Forming 2006

ISBN

83-910722-8-2

ISSN

—

e-ISSN

—

Počet stran výsledku

6

Strana od-do

77-82

Název nakladatele

Politechnika Śląska Katowice

Místo vydání

Politechnika Śląska, Katowice

Místo konání akce

—

Datum konání akce

—

Typ akce podle státní příslušnosti

—

Kód UT WoS článku

—