Microstructure of ultrafine-grained metals after ECAP

Popis výsledku v původním jazyce

This paper was aimed at verification of functionality of the ECAP technology at extrusion of the copper, alluminium alloys and steel. Experiments were made on equipment, which is demonstrated in the Fig 1. Deformation forces were measured during extrusion, resistance to deformation was calculated and deformation speed was determined approximately. Analysis of structure was made with use of light microscopy and TEM. The samples of Cu and Al alloys were extruded at room temperature. For the samples of steel was used the two-stage pressing, when the samples were extruded at temperature of approx. T1 = 325 0C and T2 = 220 0C.

Název v anglickém jazyce

Microstructure of ultrafine-grained metals after ECAP

Popis výsledku anglicky

This paper was aimed at verification of functionality of the ECAP technology at extrusion of the copper, alluminium alloys and steel. Experiments were made on equipment, which is demonstrated in the Fig 1. Deformation forces were measured during extrusion, resistance to deformation was calculated and deformation speed was determined approximately. Analysis of structure was made with use of light microscopy and TEM. The samples of Cu and Al alloys were extruded at room temperature. For the samples of steel was used the two-stage pressing, when the samples were extruded at temperature of approx. T1 = 325 0C and T2 = 220 0C.

Druh

D - Stať ve sborníku

CEP obor

JG - Hutnictví, kovové materiály

OECD FORD obor

—

Projekt

<a href="/cs/project/FI-IM%2F033" target="_blank" >FI-IM/033: Výzkum a využití nanotechnologií a výroby nanostrukturních materiálů s vysokými pevnostními vlastnostmi pro moderní konstrukce.</a><br>

Návaznosti

Z - Vyzkumny zamer (s odkazem do CEZ)

Rok uplatnění

2007

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název statě ve sborníku

11th International Research/Expert Conference "Trends in the Development of Machinery and Associated Technologies" TMT 2007

ISBN

978-9958-617-34-8

ISSN

—

e-ISSN

—

Počet stran výsledku

4

Strana od-do

1531-1534

Název nakladatele

Faculty of mechanical engineering in Zenica, Fakultetska 1, Zenica, B & H,

Místo vydání

Zenica

Místo konání akce

—

Datum konání akce

—

Typ akce podle státní příslušnosti

—

Kód UT WoS článku

—