Influence of Cooling Rate on Microstructure of a NB-V HSLA steel.
Popis výsledku v původním jazyce
In most cases an effort is made to combine controlled rolling of HSLA steel with its accelerated cooling, which has a favourable influence on mainly size of the resulting ferritic grain. In laboratory experiments mentioned below a simplified simulation of rolling of universal mill plates in a three-high mill was carried out, where slowed down cooling of final rolled products was used (given by temperature conditions in operation when rolled products are not water-sprayed and they cool from the finishingrolling temperature in collection pits).
Název v anglickém jazyce
Influence of Cooling Rate on Microstructure of a NB-V HSLA steel.
Popis výsledku anglicky
In most cases an effort is made to combine controlled rolling of HSLA steel with its accelerated cooling, which has a favourable influence on mainly size of the resulting ferritic grain. In laboratory experiments mentioned below a simplified simulation of rolling of universal mill plates in a three-high mill was carried out, where slowed down cooling of final rolled products was used (given by temperature conditions in operation when rolled products are not water-sprayed and they cool from the finishingrolling temperature in collection pits).

Druh
J<sub>x</sub> - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)
CEP obor
JG - Hutnictví, kovové materiály
OECD FORD obor
—

Rok uplatnění
2007
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Podobné výsledky(10)