CONTRIBUTION TO THE PHYSICAL METALLURGY ANALYSIS OF NEW HIGH - STRENGTH Mn ALLOYS

Popis výsledku v původním jazyce

High manganese alloys represents the perspective generation of ductile high strength material. The extraordinary mechanical properties of this alloy type come from two main features, basically: a) full FCC microstructure at required temperatures b) twinning is the main deformation mechanism. The investigated alloy (Fe-22Mn-0.6) has low stacking fault energy (SFE), which makes possible the multiple simultaneous and/or sequentional deformation mechanisms. Mechanical twinning and -martensite formation arecompetitive deformation processes which are linked to SFE. The critical value of this parameter is 18mJ/m2. In case of lower SFE the -martensite is formed preferentially. At higher SFE the twinning is detected. In case of twinning deformation process, the achieved results are: Rp = 500MPa, Rm = 1100MPa, total elongation is 5060% by practically the same level of uniform elongation. The necking formation is suppressed in this case. The impact resistance of the TWIP alloy is very beneficial

Název v anglickém jazyce

CONTRIBUTION TO THE PHYSICAL METALLURGY ANALYSIS OF NEW HIGH - STRENGTH Mn ALLOYS

Popis výsledku anglicky

High manganese alloys represents the perspective generation of ductile high strength material. The extraordinary mechanical properties of this alloy type come from two main features, basically: a) full FCC microstructure at required temperatures b) twinning is the main deformation mechanism. The investigated alloy (Fe-22Mn-0.6) has low stacking fault energy (SFE), which makes possible the multiple simultaneous and/or sequentional deformation mechanisms. Mechanical twinning and -martensite formation arecompetitive deformation processes which are linked to SFE. The critical value of this parameter is 18mJ/m2. In case of lower SFE the -martensite is formed preferentially. At higher SFE the twinning is detected. In case of twinning deformation process, the achieved results are: Rp = 500MPa, Rm = 1100MPa, total elongation is 5060% by practically the same level of uniform elongation. The necking formation is suppressed in this case. The impact resistance of the TWIP alloy is very beneficial

Druh

D - Stať ve sborníku

CEP obor

JG - Hutnictví, kovové materiály

OECD FORD obor

—

Projekt

—

Návaznosti

Z - Vyzkumny zamer (s odkazem do CEZ)

Rok uplatnění

2007

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název statě ve sborníku

METAL 2007, 16. mezinárodní konference metalurgie a materiálů

ISBN

978-80-86840-33-8

ISSN

—

e-ISSN

—

Počet stran výsledku

1

Strana od-do

63-63

Název nakladatele

Tanger spol. s r.o.

Místo vydání

Ostrava

Místo konání akce

—

Datum konání akce

—

Typ akce podle státní příslušnosti

—

Kód UT WoS článku

—