Material Engineering Analysis of the Superalloy INCONEL 792-5A after a Long-term High-temperature Exposition

Popis výsledku v původním jazyce

Hot parts of turbines are often made of nickel superalloys due to extreme requirements posed on them. This concerns particularly strength at high temperatures, resistance to fatigue failure, resistance to aggressive effect of combustion products, etc. These alloys ensure high reliability and safety at their industrial exploitation. All these factors are connected with stability of microstructure at high temperature exposition. The presented article deals with analysis of material structure of the cast variant of the nickel superalloy INCONEL 792 ? 5A after long-term annealing at high-temperatures. Numerous findings were obtained, which represent technical and physical engineering background for determination of stability of investigated superalloy thatare necessary for its technical application.

Název v anglickém jazyce

Material Engineering Analysis of the Superalloy INCONEL 792-5A after a Long-term High-temperature Exposition

Popis výsledku anglicky

Hot parts of turbines are often made of nickel superalloys due to extreme requirements posed on them. This concerns particularly strength at high temperatures, resistance to fatigue failure, resistance to aggressive effect of combustion products, etc. These alloys ensure high reliability and safety at their industrial exploitation. All these factors are connected with stability of microstructure at high temperature exposition. The presented article deals with analysis of material structure of the cast variant of the nickel superalloy INCONEL 792 ? 5A after long-term annealing at high-temperatures. Numerous findings were obtained, which represent technical and physical engineering background for determination of stability of investigated superalloy thatare necessary for its technical application.

Druh

J_x - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)

CEP obor

JG - Hutnictví, kovové materiály

OECD FORD obor

—

Projekt

<a href="/cs/project/FT-TA3%2F072" target="_blank" >FT-TA3/072: Výzkum řízení procesu krystalizace vysoce náročných odlitků vyráběných metodou vytavitelného modelu s využitím numerické simulace.</a><br>

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)

Rok uplatnění

2008

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

Hutnické listy

ISSN

0018-8069

e-ISSN

—

Svazek periodika

LXI

Číslo periodika v rámci svazku

7

Stát vydavatele periodika

CZ - Česká republika

Počet stran výsledku

6

Strana od-do

—

Kód UT WoS článku

—

EID výsledku v databázi Scopus

—