Hodnocení mikrostruktury niklové superslitiny INCONEL 792-5A po dlouhodobé teplotní expozici

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F61989100%3A27360%2F08%3A00019136" target="_blank" >RIV/61989100:27360/08:00019136 - isvavai.cz</a>

Výsledek na webu

—

DOI - Digital Object Identifier

—

Jazyk výsledku

angličtina

Název v původním jazyce

EVALUATION OF MICROSTRUCTURE OF NICKEL SUPERALLOY INCONEL 792-5A AFTER LONG TERM EXPLOITATION

Popis výsledku v původním jazyce

Nickel superalloys are often uses for parts of turbines, which must work at high temperatures. It is so because this material must satisfy numerous extreme requirements. The most importants are heat resistance at high temperatures, resistance to fatiguedamage and resistance to aggresive effect of combustion products. Long term service life and reliability of superalloys must be also satisfied. All of these factors are pertinent to stability of microstructure at long term exploitation. The submitted paper is focused on structural analysis of cast superalloy INCONEL 792-5A after long time annealing at high temperatures. Several strengthening mechanisms take effect in this alloy, the main mechanism is precipitation strengthening by coherent precipitatesof intermetallic phase Ni3Al or Ni3(Al, Ti). Superalloy was comercially produced (1120 0C/2h/air + 845 0C/24h/air) and long time annealing was carried out by regimes 900 0C/1000h or 2000h, 5000h, 10 000h. The analysis of microstructure wa

Název v anglickém jazyce

EVALUATION OF MICROSTRUCTURE OF NICKEL SUPERALLOY INCONEL 792-5A AFTER LONG TERM EXPLOITATION

Popis výsledku anglicky

Nickel superalloys are often uses for parts of turbines, which must work at high temperatures. It is so because this material must satisfy numerous extreme requirements. The most importants are heat resistance at high temperatures, resistance to fatiguedamage and resistance to aggresive effect of combustion products. Long term service life and reliability of superalloys must be also satisfied. All of these factors are pertinent to stability of microstructure at long term exploitation. The submitted paper is focused on structural analysis of cast superalloy INCONEL 792-5A after long time annealing at high temperatures. Several strengthening mechanisms take effect in this alloy, the main mechanism is precipitation strengthening by coherent precipitatesof intermetallic phase Ni3Al or Ni3(Al, Ti). Superalloy was comercially produced (1120 0C/2h/air + 845 0C/24h/air) and long time annealing was carried out by regimes 900 0C/1000h or 2000h, 5000h, 10 000h. The analysis of microstructure wa

Druh

D - Stať ve sborníku

CEP obor

JG - Hutnictví, kovové materiály

OECD FORD obor

—

Projekt

<a href="/cs/project/FT-TA3%2F072" target="_blank" >FT-TA3/072: Výzkum řízení procesu krystalizace vysoce náročných odlitků vyráběných metodou vytavitelného modelu s využitím numerické simulace.</a><br>

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)

Rok uplatnění

2008

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název statě ve sborníku

The 13th International Conference on Problems of Material Engineering, Mechanics and Design

ISBN

978-80-969728-2-1

ISSN

—

e-ISSN

—

Počet stran výsledku

1

Strana od-do

—

Název nakladatele

Alexander Dubček University of Trenčín

Místo vydání

fpt Púchov, Slovensko

Místo konání akce

—

Datum konání akce

—

Typ akce podle státní příslušnosti

—

Kód UT WoS článku

—