TiAl-Nb based alloy prepared by mechanical alloying
Popis výsledku v původním jazyce
The aim of this work was to prepare TiAl-Nb based intermetallic alloy using mechanical alloying. The compacted and sintered alloy had the mean content of 42 weight % Ti, 18 weight % Al, 19 weight % Nb. In the microstructure, the (Nb, Ti)2Al phase with 82weight % Nb, 14 weight % Al and 4 weight % Ti was found. The great amount of oxygen was determined that was in relation with the large-scale oxidation of the feet powder material.
Název v anglickém jazyce
TiAl-Nb based alloy prepared by mechanical alloying
Popis výsledku anglicky
The aim of this work was to prepare TiAl-Nb based intermetallic alloy using mechanical alloying. The compacted and sintered alloy had the mean content of 42 weight % Ti, 18 weight % Al, 19 weight % Nb. In the microstructure, the (Nb, Ti)2Al phase with 82weight % Nb, 14 weight % Al and 4 weight % Ti was found. The great amount of oxygen was determined that was in relation with the large-scale oxidation of the feet powder material.

Rok uplatnění
2008
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název statě ve sborníku
Proceeding of the 18th Joint Seminar "Development of Materials Science in Research and Education"
ISBN
978-80-254-0864-3
ISSN
—
e-ISSN
—
Počet stran výsledku
2
Strana od-do
—
Název nakladatele
Czech and Slovak Crystallographic Association
Místo vydání
Praha
Místo konání akce
Hnanice
Datum konání akce
2. 9. 2008
Typ akce podle státní příslušnosti
EUR - Evropská akce
Kód UT WoS článku
—

Podobné výsledky(10)