TiAl-Nb based alloy prepared by mechanical alloying

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F61989100%3A27360%2F10%3A86075716" target="_blank" >RIV/61989100:27360/10:86075716 - isvavai.cz</a>

Výsledek na webu

—

DOI - Digital Object Identifier

—

Jazyk výsledku

angličtina

Název v původním jazyce

TiAl-Nb based alloy prepared by mechanical alloying

Popis výsledku v původním jazyce

A possibility of preparation of TiAl-Nb based alloy using mechanical alloying in ball planetary mill was studied. Experimental material Ti-45Al-10Nb was prepared from Ti and Al powders and cut Nb wire of 0.24 mm diameter. The Ti-Al-Nb powder mixture wasmilled during 72 hours at the rate of 150 rpm. Statistic distribution of powder particle size was determined using laser particle sizer. The compacted and sintered alloy had the average content of 42.74 wt.% Ti, 19.29 wt.% Al and 19.75 wt.% Nb. In the microstructure, the phases based on Nb-Ti-Al or Nb-Ti-Al-O (with 81.3 wt. % Nb, 14.0 wt. % Al and 3.7 wt. % Ti or with 35.3 wt. % Nb, 28.8 wt. % Al, 26.7 wt. % Ti and 8.8 wt. % O, respectively) were found. Large amount of oxygen in the sintered alloy was determined. Microhardness values showed an important fluctuation in relation to inhomogeneity in chemical composition.

Název v anglickém jazyce

TiAl-Nb based alloy prepared by mechanical alloying

Popis výsledku anglicky

A possibility of preparation of TiAl-Nb based alloy using mechanical alloying in ball planetary mill was studied. Experimental material Ti-45Al-10Nb was prepared from Ti and Al powders and cut Nb wire of 0.24 mm diameter. The Ti-Al-Nb powder mixture wasmilled during 72 hours at the rate of 150 rpm. Statistic distribution of powder particle size was determined using laser particle sizer. The compacted and sintered alloy had the average content of 42.74 wt.% Ti, 19.29 wt.% Al and 19.75 wt.% Nb. In the microstructure, the phases based on Nb-Ti-Al or Nb-Ti-Al-O (with 81.3 wt. % Nb, 14.0 wt. % Al and 3.7 wt. % Ti or with 35.3 wt. % Nb, 28.8 wt. % Al, 26.7 wt. % Ti and 8.8 wt. % O, respectively) were found. Large amount of oxygen in the sintered alloy was determined. Microhardness values showed an important fluctuation in relation to inhomogeneity in chemical composition.

Druh

J_x - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)

CEP obor

JG - Hutnictví, kovové materiály

OECD FORD obor

—

Projekt

—

Návaznosti

Z - Vyzkumny zamer (s odkazem do CEZ)<br>S - Specificky vyzkum na vysokych skolach

Rok uplatnění

2010

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

Hutnické listy

ISSN

0018-8069

e-ISSN

—

Svazek periodika

63

Číslo periodika v rámci svazku

1

Stát vydavatele periodika

CZ - Česká republika

Počet stran výsledku

4

Strana od-do

23-26

Kód UT WoS článku

—

EID výsledku v databázi Scopus

—