Some Mechanical and Corrosion Aspects of Chosen TWIP Alloy

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F61989100%3A27360%2F10%3A10225290" target="_blank" >RIV/61989100:27360/10:10225290 - isvavai.cz</a>

Výsledek na webu

—

DOI - Digital Object Identifier

—

Jazyk výsledku

angličtina

Název v původním jazyce

Some Mechanical and Corrosion Aspects of Chosen TWIP Alloy

Popis výsledku v původním jazyce

The work deals with corrosion resistance of high manganese alloy of the TWIP type. The Fe22.3Mn0.5C was cast, heat treated at 1200°C/4h/water and forged with total deformation of 25% (the TWIP 1). The TWIP 2 represents the TWIP 1 re-heated at 1150°C/3h/air. Final bars corresponded to 12 mm in diameter. The Fe23.1Mn0.73C was laboratory rolled with the final strip thickness of 3 mm (TWIP 3). Exposition of all variants in the 3.5% water NaCl solution showed corrosion primarily on the boundaries of the twins. The TWIP 3 demonstrated higher corrosion resistance. The worst corrosion attack showed the TWIP 2, where the corrosion traces reached 0.12 mm under surface. The results were confronted with austenite grain sizes, formed twins and mechanical properties.

Název v anglickém jazyce

Some Mechanical and Corrosion Aspects of Chosen TWIP Alloy

Popis výsledku anglicky

The work deals with corrosion resistance of high manganese alloy of the TWIP type. The Fe22.3Mn0.5C was cast, heat treated at 1200°C/4h/water and forged with total deformation of 25% (the TWIP 1). The TWIP 2 represents the TWIP 1 re-heated at 1150°C/3h/air. Final bars corresponded to 12 mm in diameter. The Fe23.1Mn0.73C was laboratory rolled with the final strip thickness of 3 mm (TWIP 3). Exposition of all variants in the 3.5% water NaCl solution showed corrosion primarily on the boundaries of the twins. The TWIP 3 demonstrated higher corrosion resistance. The worst corrosion attack showed the TWIP 2, where the corrosion traces reached 0.12 mm under surface. The results were confronted with austenite grain sizes, formed twins and mechanical properties.

Druh

J_x - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)

CEP obor

JG - Hutnictví, kovové materiály

OECD FORD obor

—

Projekt

<a href="/cs/project/ED0040%2F01%2F01" target="_blank" >ED0040/01/01: Regionální materiálově technologické výzkumné centrum</a><br>

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)<br>Z - Vyzkumny zamer (s odkazem do CEZ)<br>S - Specificky vyzkum na vysokych skolach

Rok uplatnění

2010

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

Hutnické listy

ISSN

0018-8069

e-ISSN

—

Svazek periodika

2010

Číslo periodika v rámci svazku

5

Stát vydavatele periodika

CZ - Česká republika

Počet stran výsledku

4

Strana od-do

—

Kód UT WoS článku

—

EID výsledku v databázi Scopus

—