THE TWIP ALLOYs RESISTANCE IN SOME CORROSION REAGENTS
Identifikátory výsledku
Kód výsledku v IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F61989100%3A27360%2F10%3A10228497" target="_blank" >RIV/61989100:27360/10:10228497 - isvavai.cz</a>
Výsledek na webu
—
DOI - Digital Object Identifier
—
Alternativní jazyky
Jazyk výsledku
angličtina
Název v původním jazyce
THE TWIP ALLOYs RESISTANCE IN SOME CORROSION REAGENTS
Popis výsledku v původním jazyce
he work deals with corrosion resistance of two high Mn alloys. After cast of the Fe22.3Mn0.5C alloy heat treated at 1200°C/4h/water and forging with total deformation of 25 % were carried out. This represents the TWIP 1 alloy. The TWIP 2 alloy is the TWIP 1 re-heated at 1150°C/3h/air. Final bars corresponded to 12 mm in diameter. Further the Fe23.1Mn0.73C alloy was laboratory rolled with the final strip thickness of 3 mm representing the TWIP 3 alloy. Exposition of all variants in the 3.5 % water NaCl solution showed corrosion on the boundaries of the twins first of all. The TWIP 3 demonstrated higher corrosion resistance. The worst corrosion attack showed the TWIP 2, where the corrosion traces reached 0.12 mm under surface. After the TWIP 3 alloy exposition in corrosion solution with bubbled hydrogen sulphide (the HIC test), no hydrogen cracks were revealed. The results were confronted with austenite grain sizes, formed twins and mechanical properties.
Název v anglickém jazyce
THE TWIP ALLOYs RESISTANCE IN SOME CORROSION REAGENTS
Popis výsledku anglicky
he work deals with corrosion resistance of two high Mn alloys. After cast of the Fe22.3Mn0.5C alloy heat treated at 1200°C/4h/water and forging with total deformation of 25 % were carried out. This represents the TWIP 1 alloy. The TWIP 2 alloy is the TWIP 1 re-heated at 1150°C/3h/air. Final bars corresponded to 12 mm in diameter. Further the Fe23.1Mn0.73C alloy was laboratory rolled with the final strip thickness of 3 mm representing the TWIP 3 alloy. Exposition of all variants in the 3.5 % water NaCl solution showed corrosion on the boundaries of the twins first of all. The TWIP 3 demonstrated higher corrosion resistance. The worst corrosion attack showed the TWIP 2, where the corrosion traces reached 0.12 mm under surface. After the TWIP 3 alloy exposition in corrosion solution with bubbled hydrogen sulphide (the HIC test), no hydrogen cracks were revealed. The results were confronted with austenite grain sizes, formed twins and mechanical properties.
Klasifikace
Druh
D - Stať ve sborníku
CEP obor
JG - Hutnictví, kovové materiály
OECD FORD obor
—
Návaznosti výsledku
Projekt
<a href="/cs/project/ED0040%2F01%2F01" target="_blank" >ED0040/01/01: Regionální materiálově technologické výzkumné centrum</a><br>
Návaznosti
P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)
Ostatní
Rok uplatnění
2010
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů
Údaje specifické pro druh výsledku
Název statě ve sborníku
METAL 2010
ISBN
978-80-87294-15-4
ISSN
—
e-ISSN
—
Počet stran výsledku
6
Strana od-do
—
Název nakladatele
TANGER s.r.o. Ostrava
Místo vydání
Ostrava
Místo konání akce
Rožnov pod Radhoštěm
Datum konání akce
20. 5. 2010
Typ akce podle státní příslušnosti
WRD - Celosvětová akce
Kód UT WoS článku
—