Effect of Heat Treatment on the Structure of IN 713LC
Identifikátory výsledku
Kód výsledku v IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F61989100%3A27360%2F10%3A86075587" target="_blank" >RIV/61989100:27360/10:86075587 - isvavai.cz</a>
Nalezeny alternativní kódy
RIV/00176109:_____/10:#0000008
Výsledek na webu
—
DOI - Digital Object Identifier
—
Alternativní jazyky
Jazyk výsledku
angličtina
Název v původním jazyce
Effect of Heat Treatment on the Structure of IN 713LC
Popis výsledku v původním jazyce
Long term service life and material reliability is directly linked to its microstructure, or with its stability at long-term exploitation. These materials are usually alloyed in a complex manner and they are very complicated from structural viewpoint [1,3,8]. Superalloy was commercially produced and was investigated by use of light microscopy (LM) OLYMPUS IX 71, local chemical microanalysis and scanning electron microscopy (SEM) JEOL 6490 LV. The optimum heat treatment (HT) was found. The reached results enabled to recommend the optimum heat treatment including heating on the 1240 °C with 2 hours temperature dwell, so that precipitates dissolved completely at the grain boundaries. Subsequently, slow cooling down to the temperature of 940-950 °C leads to intensive intragranular precipitation of intermetallic phase.
Název v anglickém jazyce
Effect of Heat Treatment on the Structure of IN 713LC
Popis výsledku anglicky
Long term service life and material reliability is directly linked to its microstructure, or with its stability at long-term exploitation. These materials are usually alloyed in a complex manner and they are very complicated from structural viewpoint [1,3,8]. Superalloy was commercially produced and was investigated by use of light microscopy (LM) OLYMPUS IX 71, local chemical microanalysis and scanning electron microscopy (SEM) JEOL 6490 LV. The optimum heat treatment (HT) was found. The reached results enabled to recommend the optimum heat treatment including heating on the 1240 °C with 2 hours temperature dwell, so that precipitates dissolved completely at the grain boundaries. Subsequently, slow cooling down to the temperature of 940-950 °C leads to intensive intragranular precipitation of intermetallic phase.
Klasifikace
Druh
D - Stať ve sborníku
CEP obor
JG - Hutnictví, kovové materiály
OECD FORD obor
—
Návaznosti výsledku
Projekt
Výsledek vznikl pri realizaci vícero projektů. Více informací v záložce Projekty.
Návaznosti
P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)<br>Z - Vyzkumny zamer (s odkazem do CEZ)
Ostatní
Rok uplatnění
2010
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů
Údaje specifické pro druh výsledku
Název statě ve sborníku
METAL 2010
ISBN
978-80-87294-17-8
ISSN
—
e-ISSN
—
Počet stran výsledku
5
Strana od-do
—
Název nakladatele
TANGER, spol. s r.o.
Místo vydání
Ostrava
Místo konání akce
Rožnov p. Radhoštěm
Datum konání akce
18. 5. 2010
Typ akce podle státní příslušnosti
WRD - Celosvětová akce
Kód UT WoS článku
—