Phase Analysis of Nickel Superalloy INCONEL 738 LC
Popis výsledku v původním jazyce
The submitted paper is oriented on materials engineering investigation of microstructural characteristics of cast nickel superalloy INCONEL 738 LC (hereinafter IN) after heat treatment to the required quality and after long term annealing at the temperature of 850 oC within interval of 100 - 10 000 hours. Higher level of alloying of investigated nickel superalloy shows higher level of segregation activity, which can lead at exploitation to development of specific microsegregation processes connected with possible precipitation process and with creation of either carbidic or some variants of intermetallic phases. Several strengthening mechanisms takes place here, and main strengthening is precipitation strengthening by coherent precipitates of intermetallic phase Ni3Al, or Ni3(Ti,Al).
Název v anglickém jazyce
Phase Analysis of Nickel Superalloy INCONEL 738 LC
Popis výsledku anglicky
The submitted paper is oriented on materials engineering investigation of microstructural characteristics of cast nickel superalloy INCONEL 738 LC (hereinafter IN) after heat treatment to the required quality and after long term annealing at the temperature of 850 oC within interval of 100 - 10 000 hours. Higher level of alloying of investigated nickel superalloy shows higher level of segregation activity, which can lead at exploitation to development of specific microsegregation processes connected with possible precipitation process and with creation of either carbidic or some variants of intermetallic phases. Several strengthening mechanisms takes place here, and main strengthening is precipitation strengthening by coherent precipitates of intermetallic phase Ni3Al, or Ni3(Ti,Al).
Klasifikace
Druh
J<sub>x</sub> - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)
CEP obor
JG - Hutnictví, kovové materiály
OECD FORD obor
—
Návaznosti výsledku
Projekt
—
Návaznosti
V - Vyzkumna aktivita podporovana z jinych verejnych zdroju
Ostatní
Rok uplatnění
2010
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů
Údaje specifické pro druh výsledku
Název periodika
Communications - Scientific Letters of the University of Zilina
ISSN
1335-4205
e-ISSN
—
Svazek periodika
12
Číslo periodika v rámci svazku
4
Stát vydavatele periodika
SK - Slovenská republika
Počet stran výsledku
5
Strana od-do
—
Kód UT WoS článku
—
EID výsledku v databázi Scopus
—