Influence of Finish-rolling Temperature and Cooling Conditions on Properties of Ti-IF Steel Strip
Identifikátory výsledku
Kód výsledku v IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F61989100%3A27360%2F10%3A86075770" target="_blank" >RIV/61989100:27360/10:86075770 - isvavai.cz</a>
Výsledek na webu
—
DOI - Digital Object Identifier
—
Alternativní jazyky
Jazyk výsledku
angličtina
Název v původním jazyce
Influence of Finish-rolling Temperature and Cooling Conditions on Properties of Ti-IF Steel Strip
Popis výsledku v původním jazyce
Influence of the finish rolling temperature and cooling rate on properties of strip from IF steel, microalloyed by titanium, was investigated in laboratory conditions. The finish rolling temperatures ranging from 1000 to 770 °C covered forming in the region of austenite, ferrite, as well as forming in the two-phase region. Cooling from the finish rolling temperature was realized either in the free air, or in a slowed-down way by charging into the furnace, heated to 630 °C for a period of 15 minutes. Theevolution of recrystallization and size of the resulting ferritic grains were determined by the metallographic analysis. The strength and plastic properties of strips were evaluated by the tensile test in the room temperature. Further, influence of temperature and the annealing time, necessary for the progression of recrystallization, was evaluated in the case of selected specimens.
Název v anglickém jazyce
Influence of Finish-rolling Temperature and Cooling Conditions on Properties of Ti-IF Steel Strip
Popis výsledku anglicky
Influence of the finish rolling temperature and cooling rate on properties of strip from IF steel, microalloyed by titanium, was investigated in laboratory conditions. The finish rolling temperatures ranging from 1000 to 770 °C covered forming in the region of austenite, ferrite, as well as forming in the two-phase region. Cooling from the finish rolling temperature was realized either in the free air, or in a slowed-down way by charging into the furnace, heated to 630 °C for a period of 15 minutes. Theevolution of recrystallization and size of the resulting ferritic grains were determined by the metallographic analysis. The strength and plastic properties of strips were evaluated by the tensile test in the room temperature. Further, influence of temperature and the annealing time, necessary for the progression of recrystallization, was evaluated in the case of selected specimens.
Klasifikace
Druh
J<sub>x</sub> - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)
CEP obor
JG - Hutnictví, kovové materiály
OECD FORD obor
—
Návaznosti výsledku
Projekt
—
Návaznosti
Z - Vyzkumny zamer (s odkazem do CEZ)
Ostatní
Rok uplatnění
2010
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů
Údaje specifické pro druh výsledku
Název periodika
Hutnické listy
ISSN
0018-8069
e-ISSN
—
Svazek periodika
63
Číslo periodika v rámci svazku
4
Stát vydavatele periodika
CZ - Česká republika
Počet stran výsledku
4
Strana od-do
82-85
Kód UT WoS článku
—
EID výsledku v databázi Scopus
—