Selected Properties of Joint and its Close Neighbourhood of Stainless Steel Welded with Titanium

Popis výsledku v původním jazyce

Weld and its close neighbourhood of stainless steel with titanium of commercial purity were investigated. In vicinity of join line and 3mm away the bonding line grain size was measured both in as join condition and after annealing (600°C/1h/air). Ratio of the deformed matrix in the area of wave crest and wave trough were determined as well as the micro-hardness (HV0.1) in the mentioned areas. Differences between matrixes and interface were ascribed to presence of intermetallic phases. Toughness tests were also part of solution. Material was in as clad state and also after heat treatment, which was reason of higher sevice life.

Název v anglickém jazyce

Selected Properties of Joint and its Close Neighbourhood of Stainless Steel Welded with Titanium

Popis výsledku anglicky

Weld and its close neighbourhood of stainless steel with titanium of commercial purity were investigated. In vicinity of join line and 3mm away the bonding line grain size was measured both in as join condition and after annealing (600°C/1h/air). Ratio of the deformed matrix in the area of wave crest and wave trough were determined as well as the micro-hardness (HV0.1) in the mentioned areas. Differences between matrixes and interface were ascribed to presence of intermetallic phases. Toughness tests were also part of solution. Material was in as clad state and also after heat treatment, which was reason of higher sevice life.

Druh

J_x - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)

CEP obor

JG - Hutnictví, kovové materiály

OECD FORD obor

—

Projekt

<a href="/cs/project/ED0040%2F01%2F01" target="_blank" >ED0040/01/01: Regionální materiálově technologické výzkumné centrum</a><br>

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)<br>Z - Vyzkumny zamer (s odkazem do CEZ)

Rok uplatnění

2011

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

Hutnické listy

ISSN

0018-8069

e-ISSN

—

Svazek periodika

64

Číslo periodika v rámci svazku

6

Stát vydavatele periodika

CZ - Česká republika

Počet stran výsledku

4

Strana od-do

40-43

Kód UT WoS článku

—

EID výsledku v databázi Scopus

—