Strengthening of Two Different High Manganese Steels by K-carbides

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F61989100%3A27360%2F11%3A86079291" target="_blank" >RIV/61989100:27360/11:86079291 - isvavai.cz</a>

Nalezeny alternativní kódy

RIV/61989100:27710/11:86079291

Výsledek na webu

—

DOI - Digital Object Identifier

—

Jazyk výsledku

angličtina

Název v původním jazyce

Strengthening of Two Different High Manganese Steels by K-carbides

Popis výsledku v původním jazyce

Two different high manganese steels (X120MnAl24-12 and X70MnAl28-9) were hot rolled under the same conditions. After rolling the first steel (X120) showed inter-granularly excluded coarser k-carbides (up to micron size) unlike the second steel (X70). Thedifferences of aluminium, carbon and manganese contents showed important dissimilarity of hardness values. In steel X70 progressive k-carbides precipitation both of nano- and of mikro-size after aging at 500°C during 6, 20, 30 and 60 minutes put into effect. Detected increasing hardness (HV30) and the X-ray analysis proved it. Part of solution was also evaluation of grain sizes and stacking fault energy levels.

Název v anglickém jazyce

Strengthening of Two Different High Manganese Steels by K-carbides

Popis výsledku anglicky

Two different high manganese steels (X120MnAl24-12 and X70MnAl28-9) were hot rolled under the same conditions. After rolling the first steel (X120) showed inter-granularly excluded coarser k-carbides (up to micron size) unlike the second steel (X70). Thedifferences of aluminium, carbon and manganese contents showed important dissimilarity of hardness values. In steel X70 progressive k-carbides precipitation both of nano- and of mikro-size after aging at 500°C during 6, 20, 30 and 60 minutes put into effect. Detected increasing hardness (HV30) and the X-ray analysis proved it. Part of solution was also evaluation of grain sizes and stacking fault energy levels.

Druh

J_x - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)

CEP obor

JG - Hutnictví, kovové materiály

OECD FORD obor

—

Projekt

<a href="/cs/project/ED0040%2F01%2F01" target="_blank" >ED0040/01/01: Regionální materiálově technologické výzkumné centrum</a><br>

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)<br>Z - Vyzkumny zamer (s odkazem do CEZ)

Rok uplatnění

2011

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

Hutnické listy

ISSN

0018-8069

e-ISSN

—

Svazek periodika

64

Číslo periodika v rámci svazku

6

Stát vydavatele periodika

CZ - Česká republika

Počet stran výsledku

4

Strana od-do

36-39

Kód UT WoS článku

—

EID výsledku v databázi Scopus

—