Structural and Mechanical Properties of Laboratory Rolled Steels High-Alloyed with Mn and Al

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F61989100%3A27360%2F11%3A86079889" target="_blank" >RIV/61989100:27360/11:86079889 - isvavai.cz</a>

Výsledek na webu

—

DOI - Digital Object Identifier

—

Jazyk výsledku

angličtina

Název v původním jazyce

Structural and Mechanical Properties of Laboratory Rolled Steels High-Alloyed with Mn and Al

Popis výsledku v původním jazyce

The paper deals with rolling conditions, microstructure, as well as basic mechanical properties of four different high manganese steels after laboratory melting, casting, hot and cold rolling. The stacking fault energy of heats was in interval of 85 ? 114 mJ.m-2 thanks to the high aluminium contents. The heats with the lowest sum of (C+Mn) supported the highest ferrite fraction (up to 45 %), while the highest sum of (C+Mn) led to 10 % ferrite formation. With lower Al/(C+Mn) ratio and lower ferrite fraction the higher rolling forces were necessary to use. Due to heterogeneities of matrixes and observed aluminium oxide complexes differences in mechanical properties were detected. The best results showed the heat with 0.65 % C ? 29.5 % Mn ? 9.0 % A and stacking fault energy 114 mJ.m-2.

Název v anglickém jazyce

Structural and Mechanical Properties of Laboratory Rolled Steels High-Alloyed with Mn and Al

Popis výsledku anglicky

The paper deals with rolling conditions, microstructure, as well as basic mechanical properties of four different high manganese steels after laboratory melting, casting, hot and cold rolling. The stacking fault energy of heats was in interval of 85 ? 114 mJ.m-2 thanks to the high aluminium contents. The heats with the lowest sum of (C+Mn) supported the highest ferrite fraction (up to 45 %), while the highest sum of (C+Mn) led to 10 % ferrite formation. With lower Al/(C+Mn) ratio and lower ferrite fraction the higher rolling forces were necessary to use. Due to heterogeneities of matrixes and observed aluminium oxide complexes differences in mechanical properties were detected. The best results showed the heat with 0.65 % C ? 29.5 % Mn ? 9.0 % A and stacking fault energy 114 mJ.m-2.

Druh

D - Stať ve sborníku

CEP obor

JG - Hutnictví, kovové materiály

OECD FORD obor

—

Projekt

<a href="/cs/project/ED0040%2F01%2F01" target="_blank" >ED0040/01/01: Regionální materiálově technologické výzkumné centrum</a><br>

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)<br>Z - Vyzkumny zamer (s odkazem do CEZ)

Rok uplatnění

2011

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název statě ve sborníku

Steel Strip 2011 : the 8th international conference : conference proceedings

ISBN

978-80-260-0539-1

ISSN

—

e-ISSN

—

Počet stran výsledku

8

Strana od-do

195-202

Název nakladatele

Společnost ocelové pásy

Místo vydání

Ostrava

Místo konání akce

Stará Lesná

Datum konání akce

4. 10. 2011

Typ akce podle státní příslušnosti

WRD - Celosvětová akce

Kód UT WoS článku

—