Structural and mechanical properties of laboratory rolled steels high-alloyed with manganium and aluminium

Popis výsledku v původním jazyce

The paper deals with rolling conditions, microstructure, as well as basic mechanical properties of four different high manganese steels after laboratory melting, casting, hot and cold rolling. The stacking fault energy of heats was in interval of 85 ? 114 mJ.m-2 thanks to the high aluminium contents. The heats with the lowest sum of (C+Mn) supported the highest ferrite fraction (up to 45 %), while the highest sum of (C+Mn) led to 10 % ferrite formation. With lower Al/(C+Mn) ratio and lower ferrite fraction the higher rolling forces were necessary to use. Due to heterogeneities of matrixes and observed aluminium oxide complexes differences in mechanical properties were detected. The best results showed the heat with 0.65 % C ? 29.5 % Mn ? 9.0 % A and stacking fault energy 114 mJ.m-2.

Název v anglickém jazyce

Structural and mechanical properties of laboratory rolled steels high-alloyed with manganium and aluminium

Popis výsledku anglicky

The paper deals with rolling conditions, microstructure, as well as basic mechanical properties of four different high manganese steels after laboratory melting, casting, hot and cold rolling. The stacking fault energy of heats was in interval of 85 ? 114 mJ.m-2 thanks to the high aluminium contents. The heats with the lowest sum of (C+Mn) supported the highest ferrite fraction (up to 45 %), while the highest sum of (C+Mn) led to 10 % ferrite formation. With lower Al/(C+Mn) ratio and lower ferrite fraction the higher rolling forces were necessary to use. Due to heterogeneities of matrixes and observed aluminium oxide complexes differences in mechanical properties were detected. The best results showed the heat with 0.65 % C ? 29.5 % Mn ? 9.0 % A and stacking fault energy 114 mJ.m-2.

Druh

J_x - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)

CEP obor

JG - Hutnictví, kovové materiály

OECD FORD obor

—

Projekt

<a href="/cs/project/ED0040%2F01%2F01" target="_blank" >ED0040/01/01: Regionální materiálově technologické výzkumné centrum</a><br>

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)<br>S - Specificky vyzkum na vysokych skolach

Rok uplatnění

2012

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

Archives of Civil and Mechanical Engineering

ISSN

1644-9665

e-ISSN

—

Svazek periodika

12

Číslo periodika v rámci svazku

3

Stát vydavatele periodika

PL - Polská republika

Počet stran výsledku

6

Strana od-do

312-317

Kód UT WoS článku

—

EID výsledku v databázi Scopus

—