Evolution of the microstructure and mechanical properties of AlSiMg alloy during Equal Channel Angular Pressing

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F61989100%3A27360%2F11%3A86081190" target="_blank" >RIV/61989100:27360/11:86081190 - isvavai.cz</a>

Výsledek na webu

—

DOI - Digital Object Identifier

—

Jazyk výsledku

angličtina

Název v původním jazyce

Evolution of the microstructure and mechanical properties of AlSiMg alloy during Equal Channel Angular Pressing

Popis výsledku v původním jazyce

A commercial AISiMg aluminum alloy was processed by Equal Channel Angular Pressing at room temperature to a strain of ~ 7. The as-extruded microstructure is quite uniform, which can be characterized as a mixture of elongated and equiaxed subgrains with submicrometer size and high misorientations. In static annealing, the as- extruded structure is quite stable at 150°C and shows slow coarsening at 200°C. The microstructure resulted from more ECAP passes is more readily to develop a uniform structure of equiaxed grains in static annealing. High strength (275 MPa yield stress and 340 MPa ultimate tensile strength) and ductility (5.5% tensile elongation) can be obtained in this AISiMg aluminum alloy. The high strength can be related to the structure of submicron-sized sub- grains (grains). To increase the strain from 4 to 7 is beneficial for producing finer structure and higher strength.

Název v anglickém jazyce

Evolution of the microstructure and mechanical properties of AlSiMg alloy during Equal Channel Angular Pressing

Popis výsledku anglicky

A commercial AISiMg aluminum alloy was processed by Equal Channel Angular Pressing at room temperature to a strain of ~ 7. The as-extruded microstructure is quite uniform, which can be characterized as a mixture of elongated and equiaxed subgrains with submicrometer size and high misorientations. In static annealing, the as- extruded structure is quite stable at 150°C and shows slow coarsening at 200°C. The microstructure resulted from more ECAP passes is more readily to develop a uniform structure of equiaxed grains in static annealing. High strength (275 MPa yield stress and 340 MPa ultimate tensile strength) and ductility (5.5% tensile elongation) can be obtained in this AISiMg aluminum alloy. The high strength can be related to the structure of submicron-sized sub- grains (grains). To increase the strain from 4 to 7 is beneficial for producing finer structure and higher strength.

Druh

J_x - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)

CEP obor

JG - Hutnictví, kovové materiály

OECD FORD obor

—

Projekt

<a href="/cs/project/GA106%2F09%2F1598" target="_blank" >GA106/09/1598: Výzkum vlastností a výroba nanostrukturního titanu pro dentální implantáty</a><br>

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)<br>Z - Vyzkumny zamer (s odkazem do CEZ)

Rok uplatnění

2011

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

Strojírenská technologie

ISSN

1211-4162

e-ISSN

—

Svazek periodika

16

Číslo periodika v rámci svazku

6

Stát vydavatele periodika

CZ - Česká republika

Počet stran výsledku

7

Strana od-do

6-12

Kód UT WoS článku

—

EID výsledku v databázi Scopus

—