ANALYSIS OF CHOSEN HIGH MANGANESE STEELS PARAMETERS

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F61989100%3A27360%2F12%3A86083842" target="_blank" >RIV/61989100:27360/12:86083842 - isvavai.cz</a>

Nalezeny alternativní kódy

RIV/61989100:27710/12:86083842

Výsledek na webu

—

DOI - Digital Object Identifier

—

Jazyk výsledku

angličtina

Název v původním jazyce

ANALYSIS OF CHOSEN HIGH MANGANESE STEELS PARAMETERS

Popis výsledku v původním jazyce

The work deals with four high manganese steels types with aluminium addition higher than 8 wt. %. Manganese content was lying in range of 24-29.5 wt. % and carbon was in the interval from 0.4 wt. % to 1.2 wt. %. Different levels of the above mentioned elements led to dissimilar mechanical properties and metallographic ones. All steels types were cast laboratory and the hot and cold rolling was realised using reversible laboratory rolling mill TANDEM and four-high rolling mill Q110. The work mutually compares influence of all used crucial elements of the chemical compositions, calculated stacking fault energies (SFE) and transformed d-ferrite from the basic FCC matrix. Specific balance between manganese, carbon and aluminium play an important part in k-carbides precipitation. Mechanical properties and microstructures of investigated materials are integral parts of solution. Results are confronted with accessible literature pieces of knowledge.

Název v anglickém jazyce

ANALYSIS OF CHOSEN HIGH MANGANESE STEELS PARAMETERS

Popis výsledku anglicky

The work deals with four high manganese steels types with aluminium addition higher than 8 wt. %. Manganese content was lying in range of 24-29.5 wt. % and carbon was in the interval from 0.4 wt. % to 1.2 wt. %. Different levels of the above mentioned elements led to dissimilar mechanical properties and metallographic ones. All steels types were cast laboratory and the hot and cold rolling was realised using reversible laboratory rolling mill TANDEM and four-high rolling mill Q110. The work mutually compares influence of all used crucial elements of the chemical compositions, calculated stacking fault energies (SFE) and transformed d-ferrite from the basic FCC matrix. Specific balance between manganese, carbon and aluminium play an important part in k-carbides precipitation. Mechanical properties and microstructures of investigated materials are integral parts of solution. Results are confronted with accessible literature pieces of knowledge.

Druh

D - Stať ve sborníku

CEP obor

JG - Hutnictví, kovové materiály

OECD FORD obor

—

Projekt

<a href="/cs/project/ED0040%2F01%2F01" target="_blank" >ED0040/01/01: Regionální materiálově technologické výzkumné centrum</a><br>

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)

Rok uplatnění

2012

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název statě ve sborníku

METAL 2012 : 21st International Conference on Metallurgy and Materials : conference proceedings

ISBN

978-80-87294-31-4

ISSN

—

e-ISSN

—

Počet stran výsledku

6

Strana od-do

744-749

Název nakladatele

Tanger

Místo vydání

Ostrava

Místo konání akce

Brno

Datum konání akce

23. 5. 2012

Typ akce podle státní příslušnosti

WRD - Celosvětová akce

Kód UT WoS článku

—