INFLUENCE OF AGING PROCESS ON STRENGTHENING OF TREE TRIPLEX STEELS TYPES

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F61989100%3A27360%2F12%3A86083843" target="_blank" >RIV/61989100:27360/12:86083843 - isvavai.cz</a>

Výsledek na webu

—

DOI - Digital Object Identifier

—

Jazyk výsledku

angličtina

Název v původním jazyce

INFLUENCE OF AGING PROCESS ON STRENGTHENING OF TREE TRIPLEX STEELS TYPES

Popis výsledku v původním jazyce

The work deals with three high manganese steels of TRIPLEX type. Manganese was in the range of 24 to 28 wt. %, carbon in the interval of 0.2 to 1.2 wt. % and aluminium was at the level from 2.3 wt. % to 12 wt. %. Chemical composition variability, rollingconditions and following aging process realised at the temperature of 500°C and four different aging dwells including 6, 12, 20 and 60 minutes led to various k-carbides precipitation both of nano and of micro size. Chemical compositions, concretely themanganese, carbon and aluminium balances, influenced the k-carbides precipitation which was also detected using the X-ray. The main expression of the k-carbides precipitation was the investigated hardness (HV30). Mechanical properties after tensile testsand microstructure analyses are inseparable part of presented solution. All results are compared to one other and confronted with literature information.

Název v anglickém jazyce

INFLUENCE OF AGING PROCESS ON STRENGTHENING OF TREE TRIPLEX STEELS TYPES

Popis výsledku anglicky

The work deals with three high manganese steels of TRIPLEX type. Manganese was in the range of 24 to 28 wt. %, carbon in the interval of 0.2 to 1.2 wt. % and aluminium was at the level from 2.3 wt. % to 12 wt. %. Chemical composition variability, rollingconditions and following aging process realised at the temperature of 500°C and four different aging dwells including 6, 12, 20 and 60 minutes led to various k-carbides precipitation both of nano and of micro size. Chemical compositions, concretely themanganese, carbon and aluminium balances, influenced the k-carbides precipitation which was also detected using the X-ray. The main expression of the k-carbides precipitation was the investigated hardness (HV30). Mechanical properties after tensile testsand microstructure analyses are inseparable part of presented solution. All results are compared to one other and confronted with literature information.

Druh

D - Stať ve sborníku

CEP obor

JG - Hutnictví, kovové materiály

OECD FORD obor

—

Projekt

<a href="/cs/project/ED0040%2F01%2F01" target="_blank" >ED0040/01/01: Regionální materiálově technologické výzkumné centrum</a><br>

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)

Rok uplatnění

2012

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název statě ve sborníku

METAL 2012 : 21st International Conference on Metallurgy and Materials : conference proceedings

ISBN

978-80-87294-31-4

ISSN

—

e-ISSN

—

Počet stran výsledku

6

Strana od-do

750-755

Název nakladatele

Tanger

Místo vydání

Ostrava

Místo konání akce

Brno

Datum konání akce

23. 5. 2012

Typ akce podle státní příslušnosti

WRD - Celosvětová akce

Kód UT WoS článku

—